Size-dependent antimicrobial properties of sugar-encapsulated gold nanoparticles synthesized by a green method.
Jump to Full Text
MedLine Citation:
PMID:  23146145     Owner:  NLM     Status:  PubMed-not-MEDLINE    
Abstract/OtherAbstract:
The antimicrobial properties of dextrose-encapsulated gold nanoparticles (dGNPs) with average diameters of 25, 60, and 120 nm (± 5) and synthesized by green chemistry principles were investigated against both Gram-negative and Gram-positive bacteria. Studies were performed involving the effect of dGNPs on the growth, morphology, and ultrastructural properties of bacteria. dGNPs were found to have significant dose-dependent antibacterial activity which was also proportional to their size. Experiments revealed the dGNPs to be bacteriostatic as well as bactericidal. The dGNPs exhibited their bactericidal action by disrupting the bacterial cell membrane which leads to the leakage of cytoplasmic content. The overall outcome of this study suggests that green-synthesized dGNPs hold promise as a potent antibacterial agent against a wide range of disease-causing bacteria by preventing and controlling possible infections or diseases.
Authors:
Vivek D Badwaik; Lakshmisri M Vangala; Dillon S Pender; Chad B Willis; Zoraida P Aguilar; Matthew S Gonzalez; Rammohan Paripelly; Rajalingam Dakshinamurthy
Related Documents :
20800015 - Morphological changes and viability of cryptosporidium parvum sporozoites after excysta...
16419745 - Electron microscopic observation of the invasion process of cryptosporidium parvum in s...
12841355 - Decreased level of 2,3-diphosphoglycerate and alteration of structural integrity in ery...
16470415 - Multi-membrane-bound structures of apicomplexa: ii. the ovoid mitochondrial cytoplasmic...
8819665 - Morphology of spleen in steroid resistant idiopathic thrombocytopenic purpuras.
698395 - Effect of c3b inactivator on monocyte-bound c3-coated human erythrocytes.
Publication Detail:
Type:  Journal Article     Date:  2012-11-12
Journal Detail:
Title:  Nanoscale research letters     Volume:  7     ISSN:  1556-276X     ISO Abbreviation:  Nanoscale Res Lett     Publication Date:  2012  
Date Detail:
Created Date:  2013-01-01     Completed Date:  2013-01-02     Revised Date:  2013-03-13    
Medline Journal Info:
Nlm Unique ID:  101279750     Medline TA:  Nanoscale Res Lett     Country:  United States    
Other Details:
Languages:  eng     Pagination:  623     Citation Subset:  -    
Affiliation:
Department of Chemistry, Western Kentucky University, Bowling Green, KY 4210, USA. rajalingam.dakshinamurthy@wku.edu.
Export Citation:
APA/MLA Format     Download EndNote     Download BibTex
MeSH Terms
Descriptor/Qualifier:
Comments/Corrections

From MEDLINE®/PubMed®, a database of the U.S. National Library of Medicine

Full Text
Journal Information
Journal ID (nlm-ta): Nanoscale Res Lett
Journal ID (iso-abbrev): Nanoscale Res Lett
ISSN: 1931-7573
ISSN: 1556-276X
Publisher: Springer
Article Information
Download PDF
Copyright ©2012 Badwaik et al.; licensee Springer.
open-access:
Received Day: 6 Month: 8 Year: 2012
Accepted Day: 31 Month: 10 Year: 2012
collection publication date: Year: 2012
Electronic publication date: Day: 12 Month: 11 Year: 2012
Volume: 7 Issue: 1
First Page: 623 Last Page: 623
PubMed Id: 23146145
ID: 3533927
Publisher Id: 1556-276X-7-623
DOI: 10.1186/1556-276X-7-623

Size-dependent antimicrobial properties of sugar-encapsulated gold nanoparticles synthesized by a green method
Vivek D Badwaik1 Email: vivek.badwaik782@topper.wku.edu
Lakshmisri M Vangala1 Email: lakshmisri.vangala672@topper.wku.edu
Dillon S Pender1 Email: dillon.pender472@topper.wku.edu
Chad B Willis1 Email: chad.willis646@wku.edu
Zoraida P Aguilar2 Email: zaguilar@oceannanotech.com
Matthew S Gonzalez1 Email: matthew.gonzalez377@topper.wku.edu
Rammohan Paripelly1 Email: rammohan.paripelly847@topper.wku.edu
Rajalingam Dakshinamurthy1 Email: rajalingam.dakshinamurthy@wku.edu
1Department of Chemistry, Western Kentucky University, Bowling Green, KY 4210, USA
2Ocean Nano Tech, Springdale, AR 72764, USA

Background

Multidrug-resistant (MDR) bacteria represent a major threat to the success of many branches of medical sciences. Some patients are especially vulnerable of acquiring MDR bacterial infections as a consequence of treatments for illnesses such as organ transplant, hemodialysis, and various types of cancer [1]. Each year at least 150,000 people die around the world due to the infection of a particular MDR bacterium [2]. Therefore, there is an immense need for new strategies to design antibacterial agents [3].

Nanoparticles (NPs) have been used to synthesize or to improve the remedial efficacy of antibacterial agents [4-10]. NPs for this purpose are generally synthesized by using various metals and polymers [11,12]. ZnO nanoparticles have been used as an antibacterial agent but, published studies also showed that ZnO nanoparticles were toxic to T cells and neuroblastoma cells [13,14]. Copper nanoparticles have been shown as a potential antimicrobial agent, but it also comes with the cost of toxicity to eukaryotic cells e.g., potential damage to dorsal root ganglion neuron [15,16]. Similarly, silver nanoparticles have been studied extensively for their potential antibacterial properties [17], but many concerns arises over their use on mammalian cells due to the essential toxicity of silver e.g., the genotoxicity towards mammalian cell lines such as mouse embryonic stem cells and mouse embryonic fibroblasts [18,19]. The use of silver nanoparticles for medical applications is potentially limited due to their nonspecific biological toxicity. Compared to all the metal nanoparticles mentioned above, gold nanoparticles are more amenable to surface modification and are also photostable, and nontoxic based on the extensive review on nanotechnology [20,21].

Thus, where the undesirable properties such as cellular toxicity and instability of these NPs limit their application, the gold nanoparticles (GNPs) have attracted a significant interest because of their convenient surface bioconjugation, remarkable plasmon-resonant optical properties, chemical stability, and non-toxicity [22-25]. Studies have also shown that the GNPs are useful to improve the efficacy, delivery, target specificity, and biodistribution of the drugs which enhance the antibacterial activity against MDR bacteria [11-14]. However, the use of complicated non-bio/non-ecofriendly chemical synthesis processes and dependence on external sources (such as laser pulses) for the synthesis and/or the activation of GNPs limits their environmental/biocompatibility [26-30]. Moreover, the size of the GNPs strongly influences their physical, chemical, and biological properties [31,32]. Therefore, there is a need for GNPs with different sizes for various biomedical applications including those with antibacterial activity [33].

This report is focused on the antibacterial activity of the dextrose-encapsulated gold nanoparticles (dGNPs) which were synthesized by employing a ‘completely green’ method as shown in our previously published article [34]. In this context ‘green’ refers to the process in which the dGNPs were synthesized. The green process is completely natural allowing for the reproducible synthesis of differently sized dGNPs without the need for harsh chemicals or expensive equipment such as lasers. The advantages of said ‘green techniques’ are linked with natural, inexpensive, chemical stability, and ecofriendliness. Three different sizes of dGNPs were synthesized having the average diameters of 25, 60, and 120 nm (±5). The resulting dGNPs were nearly spherical, monodispersed, stable, and water soluble. The dGNPs were prepared using dextrose as both reducing and capping agent.

We explored the antibacterial activity of the dGNPs against both Gram-negative (Escherichia coli) and Gram-positive (Staphylococcus epidermidis) bacteria. Investigation of the bacterial growth kinetics and growth inhibition, in the presence of dGNPs at various concentrations, was performed using a real-time spectrophotometric assay. Antibacterial activity and efficacy were further validated by turbidimetry and spread plate assays. To understand the mechanism of action, we performed fluorescence microscopy and observed ultrathin slices of nanoparticles-treated bacterial cells under transmission electron microscope (TEM).


Methods

Chemicals including KAuCl4/HAuCl4, Luria-Bertani broth, Luria broth (LB) agar, tryptic soy agar, propidium iodide, and dextrose were purchased from Aldrich, St. Louis, MO, USA. E. coli and S. epidermidis were purchased from Invitrogen, Carlsbad, CA, USA or obtained from Western Kentucky University’s culture collection. Analytical grade chemicals were typically used.

Synthesis and characterization of dGNPs

Gold nanoparticles were synthesized according to our previously published environmentally benign, biofriendly, single-step/single-phase synthesis method [34]. In this method dextrose was used as a reducing agent as well as a capping agent causing the reduction of Au3+ ions in an aqueous buffer at room temperature and atmospheric pressure. In a typical dGNPs sample, preparation process the reaction mixture was centrifuged at 6,000 rpm for 20 min, and the supernatant was discarded. The precipitated dGNPs were resuspended in autoclaved nanopure water and then again precipitated by centrifugation (and the supernatant was discarded). This resuspension and precipitation processes were repeated at least four times and then the dGNPs samples were used for further analysis. This washing procedure helped us to make sure that the dGNPs sample does not contain any free dextrose or any free Au ions. The synthesized dGNPs were characterized using various analytical techniques including TEM analysis (Section A in Additional file 1). To determine the morphology of dGNPs, the absorption spectra were observed using Perkin Elmer Lambda 35 UV/vis spectrophotometer (Perkin Elmer Inc., Waltham, MA, USA). Energy dispersive spectroscopy was performed to analyze the elemental composition of nanoparticles using JEOL JSM 5400 LV with IXRF system (JEOL Ltd., Tokyo, Japan). Quantification of dGNPs was performed using the reported methods [3,34-38] (Section B in Additional file 1). The presence of dextrose on the surface of dGNP was further confirmed by Benedict’s test [35] (Section C in Additional file 1).The presence of hydroxyl group was determined by treatment with acetic anhydride and pyridine followed by titration with sodium hydroxide [36] (Section D Additional file 1). The more detailed experimental procedure for quantification, Benedict’s test, and volumetric titration are described in the additional word file (Additional file 1).

Determination of antibacterial activity of dGNPs

The antibacterial experiments were performed using fresh culture of bacteria obtained by inoculating 100 μL of bacterial glycerol stock into 10 mL of sterile LB or minimal liquid medium in a culture tube. The bacteria were allowed to grow overnight in an incubator maintained at 37°C and shaken at 150 rpm. For all the experiments, dGNPs were washed several times with sterile water and then resuspended in nanopure water or medium.

Turbidimetry

Turbidimetry refers to a microbiological assay performed for measuring the minimum inhibitory concentration (MIC) of dGNPs against E. coli. Various concentrations of dGNPs with average diameters of 120 nm (2 × 1010, 4 × 1010, 8 × 1010, 16 × 1010 NPs/mL), 60 nm (2 × 1011, 4 × 1011, 8 × 1011, 16 × 1011 NPs/mL), 25 nm (16 × 1012, 32 × 1012, 64 × 1012, 128 × 1012 NPs/mL) were inoculated with 1 × 106 CFU/mL in a series of culture tubes containing 4 mL of sterile liquid media. Control experiments were performed by inoculating the media with E. coli in the absence of dGNPs. All tubes were incubated at 37°C, and the growth of bacteria was monitored by measuring the optical density (OD) at 600 nm for 12 h. OD 600 is an acronym indicating the optical density of a sample measured at a wavelength of 600 nm. Optical density at 600 nm is a common method used in molecular biology to quantify the bacteria by determining the absorbance at 600 nm [39,40].

Spread plate technique

The bacteria (E. coli/S. epidermidis) were grown in a series of culture tubes containing 4 mL of sterile liquid media with various concentrations of dGNPs. Cultures from selected concentrations and growth points (12 h) were spread onto LB or tryptic soy agar plates and incubated at 37°C for 12 h to estimate the number of viable bacteria [41].

Fluorescence assay

The bacteria were cultured in liquid media in the presence of different concentrations of dGNPs for 12 h at 37°C. The samples were collected and centrifuged at 6,000 rpm for 3 min and washed twice with phosphate buffered saline (PBS, pH ~ 7.2). These bacterial cells were incubated with propidium iodide (3 μM in PBS) in the dark for 30 min at room temperature. Fluorescence detection was performed on 10 μL of the bacterial suspension that was placed on a glass slide and observed under Leica scanning fluorescence microscope (Leica Microsystems, Buffalo Grove, IL, USA) [3]. Positive control was prepared by treating the bacterial suspension with 100% ethyl alcohol for 15 min.

Preparation for cross section of the bacterial cells

Ultrastructural changes induced by dGNP treatment were studied under an electron microscope. The cultures of the two bacterial strains were fixed by mixing with equal volumes of a × 2 fixative solution to give final concentrations of 2.0% w/v paraformaldehyde and 2.5% w/v glutaraldehyde in 50 mM sodium cacodylate buffer (pH 7.4). After incubating with fixative for 2 h at room temperature, the fixed samples were washed and centrifuged twice; the supernatant was discarded, and the pellet was resuspended in 50 mM sodium cacodylate buffer. The same process was followed during all subsequent solution changes. Samples were post-fixed for 1 h at 25°C with 1% w/v osmium tetroxide in 50 mM sodium cacodylate buffer. The post-fixed samples were washed with nanopure water twice and then dehydrated in a graded ethanol series (once in 25%, 50%, 75%, and 95%, and thrice in 100% ethanol for 10 min each). The dehydrated samples were infiltrated with Spurr’s epoxy resin (once in 33%, 66%, 95%, and thrice in 100% resin for 1 h each) and then left overnight in 100% resin. The samples were centrifuged through fresh resin in BEEM capsules (BEEM Inc., West Chester, PA, USA) and hardened at 70°C for 18 h. Ultrathin sections of the pelleted samples were cut on an RMC MT-X ultra-microtome using a glass knife. The sections were stained with 2% aqueous uranyl acetate and Reynold’s lead citrate for 15 and 3 min, respectively and examined using a JEOL-100CX transmission electron microscope [42,43].


Results and discussion

Recent advances in the field of nanobiotechnology have been used for the development of new antibacterial agents. Non-bio/ non-ecofriendly synthesis processes, cellular toxicity, and instability of nanoparticles severely limit the nanoparticles application. Taking this into consideration, we explored the antibacterial properties of stable, biocompatible, ecofriendly dGNPs.

Synthesis and characterization of dGNPs

Three different sizes of dGNPs [25, 60, and 120 nm (±5)] were synthesized using the previously published method in which dextrose was used as a capping and reducing agent (see Section A in Additional file 1) [34]. The dGNPs of different sizes were produced by varying the concentrations of KAuCl4.

Antibacterial activity

In determination of the antibacterial activity of dGNPs, we performed both liquid broth and solid agar plate-based growth studies on E. coli. The dGNPs of different sizes were tested for their antibacterial activity at various concentrations against E. coli. Before performing the actual antibacterial experiment, the dGNPs were tested for their stability by suspending the nanoparticles in sterile liquid media in culture tube and kept in an incubator shaker at 37°C. The dGNPs were found to be intact/stable (no cluster/precipitation) for more than 48 h. In the tube assay, the bacterial cells were grown in the presence of dGNPs, and the growth was monitored hourly by measuring the OD at 600 nm for 12 h. Optical density at 600 nm is a common method to quantify the concentration of bacterial cells in a liquid medium. Blank samples were prepared by suspending the dGNPs in sterile liquid medium and processed in same condition as that of the samples. Any absorption due to dGNPs was autocorrected using a blank sample. Results were plotted with the OD on Y-axis against the time on X-axis (Figure 1). Both the 120-nm and 60-nm dGNPs were found to inhibit the proliferation of E. coli, in a concentration-dependent manner with MIC at 16 × 1010 and 16 × 1011 NPs/mL, respectively. The 25-nm dGNPs did not significantly affect the proliferation of E. coli even at a concentration as high as 128 × 1012 NP/mL. The 120-nm dGNPs were found to be the most potent antibacterial agent compared with the 60 nm which, in turn, were more potent than the 25 nm (Figure 1). The growth kinetic data clearly suggested that the antibacterial activity was directly proportional to the increase in the size of dGNPs.

The antibacterial activity exhibited by dGNPs could be attributed to the presence of free Au3+ ions that remained in the solution when the dGNPs were suspended in water or due to changes in pH, since the bacterial activity is sensitive to both of these factors. To quantify the free Au3+ ions in the suspension, the dGNPs precipitated by centrifugation and the supernatant was tested for the presence of free Au3+ ions by measuring the absorbance at 290 nm. The near zero absorbance at 290 nm showed the absence of any free Au3+ ion (data not shown), suggesting that the free Au3+ ions concentration in the dGNPs suspension was insignificant and therefore, not responsible for the antibacterial activity. In addition the pH of the dGNPs suspensions was near 7.2 to 7.4 which is the normal pH range for the microorganism environment. Hence, the pH could not have been responsible for the antibacterial activity. Taken together, the results suggested that the antibacterial activity was solely due to the dGNPs and not due to free Au3+ ion or changes in pH.

The results of the growth assay indicated that the presence of dGNPs inhibited the growth of E. coli, representing the bacteriostatic property of the dGNPs. In order to confirm whether dGNPs exhibited bactericidal action, spread plate technique was used. The cultures in the liquid broth that were treated with different sizes of dGNPs for 12 h [the time required by control to reach the stationary phase (complete growth)] were plated on fresh LB agar media. The results given in Figure 2A,B indicated that the number of colonies on the agar plate significantly decreased with increase in the size of dGNPs. The antibacterial potency of dGNPs increased as the size increased (25 < 60 < 120 nm). Furthermore, the growth of the colonies on the agar plate demonstrated that within one size of dGNPs, the bactericidal effect was concentration dependent (Figure 2). The above results from the agar spread plate methods confirmed that the dGNPs exhibited bactericidal properties.

dGNPs-induced disruption of bacterial cells

The process of the antibacterial activity of dGNPs was determined using time-dependent action of dGNPs on the morphology of bacterial cell and monitoring the results. This was done by collecting the dGNP-treated E. coli cells at different time points which were then processed for cross-sectional analysis. The TEM analysis of the cross sections of untreated cells showed that the membrane integrity remained intact at different time points even after the stationary phase (after 12 h) (a and b in Figure 3A). However, bacteria treated with 120 and 60 nm dGNPs showed gradual morphological changes within 6 h. Initially, the dGNPs were observed to anchor onto the surface of the cell at several sites (a in Figure 3B). Gradually, the sites where the dGNPs lodged showed the formation of perforations or outer membrane vesicles (OMVs) on the membrane, which eventually resulted into complete cell lysis (b and c in Figure 3B) [44,45].

To investigate the effect of various sizes of dGNPs on the cell permeability, cells were treated with propidium iodide (PI). PI is a fluorescent dye which specifically binds with nucleic acid and produces enhanced fluorescence. However, PI cannot cross intact membranes and is excluded from the viable cells [3]. Thus, in the presence of PI, cells with permeable membrane (lysed or damaged cell membrane) will fluoresce under the fluorescence microscope. For this study we incubated fresh E. coli cultures with different sizes of dGNPs and then treated with PI to assess the integrity of the cell membrane. Fluorescence images showed that the permeability of dGNP-treated bacteria was 92% for 120 nm, 87% for 60 nm, and very minimal permeability of less than 13% for 25 nm (Figure 4A). The permeability of the cell membrane increased significantly with exposure to increase in the size of dGNPs and also with the increase in the concentration of dGNPs (Figure 4B). Therefore, exposure of the cells to dGNPs leads to the disruption of the integrity of the cell membrane, causing increased permeability and possible leaching of the cell materials. These results indicated the size-dependent effect of the dGNPs on bacterial membrane through the time-dependent leaching/disruption. It must be noted that the mechanism of interaction between the cell membrane and the dGNPs needs to be investigated.

To determine the versatile antibacterial nature of the dGNPs, we further studied the action of dGNPs against S. epidermidis. Staphylococcus is a genus of Gram-positive bacteria, which resides normally on the skin and mucous membranes of human and other organisms causing a wide array of diseases [46-48]. Various antibacterial experiments were performed against S. epidermidis similar to those performed against E. coli. Plate-based growth studies were performed to determine the bactericidal action of dGNPs, in which the cultures in the liquid broth that were treated with different sizes of dGNPs for 12 h (complete growth) were then plated on fresh tryptic soy agar media. The results showed similarity to the results obtained against E. coli, indicating less number of recovered cells with increasing size of dGNPs as well as with increase in the concentration of particles (Figure 5). Though having antibiotic action against both species (E. coli and S. epidermidis), the process of action could be different. Therefore, to determine the process of action against S. epidermidis, TEM and fluorescence studies were performed. TEM analysis was done by collecting dGNPs-treated S. epidermidis cells at different time points and was processed for cross-sectional analysis. The morphological changes were observed through the analysis of these cross sections which clearly showed the disruption of cell membrane at the initial phase, which eventually lead to cell lysis (Figure 6). The fluorescence assay performed using PI also showed the disruption of the integrity of the cell membrane which causes increased permeability and possible leaching of the cell materials (Figure 7). Thus, the different types of antibacterial assays suggested that the antibacterial activity of dGNPs against S. epidermidis also occurred through the disruption of bacterial cellular membrane, similar to that of E. coli[48].

The overall results suggested similar potency and membrane disruption process for the antibacterial activity of dGNPs towards Gram-negative as well as Gram-positive bacteria. Dextrose is a polyhydroxylated molecule, which can act both as a hydrogen bond donor as well as a hydrogen bond acceptor. The presence of the capping ligand dextrose was confirmed with positive Benedict’s test (Section C in Additional file 1). The hydroxyl group was also detected using acetylation reaction followed by volumetric titration with sodium hydroxide (Section D in Additional file 1). The presence of hydroxyl group can thus be attributed for the strong electrostatic interaction between dGNPs and both Gram-negative or Gram-positive bacteria, which in turn lead to the disruption of cell membrane. Thus, this may explain the versatile antibacterial activity of these dGNPs. It may be inferred that the ligand molecule dextrose plays a crucial role in the antibacterial action but the mechanism of interaction remains to be established.


Conclusions

In this present work, we have investigated the antibacterial activity of biofriendly/ecofriendly dextrose-encapsulated GNPs of sizes 25, 60, and 120 nm (± 5). These green-synthesized dGNPs showed significant antibacterial activity against both Gram-negative as well as Gram-positive bacteria. The efficiency of antibacterial activity was directly proportional to the increase in size as well as the concentration of dGNPs. These dGNPs were found to exert their antibacterial action via disruption of the cell membrane leading to possible leakage of the cytoplasmic contents including nucleic acids. Based on the results, it is plausible that the amphoteric nature of dextrose (the capping ligand) might be responsible for the interaction of dGNPs with both the Gram-positive and Gram-negative bacteria which, in turn, leads to the antibacterial activity. The antibacterial properties of the dGNPs hold promise for pharmaceutical, disinfectant, and other biomedical applications. The molecular level interaction between the cell membrane and the dGNPs that causes membrane rupture remains to be established.


Competing interests

The authors declare that they have no competing interests.


Authors’ contributions

VDB, LMV, DP, CW, and DR synthesized the different sizes of GNPs. VDB, LMV, CW, ZA, and DR characterized GNPs using TEM and performed UV/vis spectroscopy and all the antibacterial assays. All authors read and approved the final manuscript.


Supplementary Material Additional file 1

Detailed description of the experimental procedures for quantification, Benedict’s test, and volumetric titration. The additional file 1 contains the TEM images for three different sizes of dGNPs along with the description of quantification of dGNPs. The presence of dextrose on the surface of dGNPs was determined using the Benedict’s test which has been discussed along with the experimental results. Moreover, the additional file contains a brief discussion over the volumetric titration that was performed to determine the presence of unreduced hydroxyl group.


Click here for additional data file (1556-276X-7-623-S1.docx)


Acknowledgments

We are grateful to Dr. John Andersland for TEM analysis. The project was supported in part by Department of Chemistry, Advanced Materials Institute, Ogden College of Science and Engineering, Office of Sponsored Programs at Western Kentucky University and grants from the National Center for Research Resources (5P20RR016481-12) and the National Institute of General Medical Sciences (8 P20 GM103436-12) from the National Institutes of Health and National Science Foundation Research Experience for Undergraduates (REU) grant number EAR-1004655. The honors college grant to DSP and the graduate student research grants to VDB and LMV are also appreciated.


References
So AD,Gupta N,Brahmachari SK,Chopra I,Munos B,Nathan C,Outterson K,Paccaud JP,Payne DJ,Peeling RW,Spigelman M,Weigelt J,Towards new business models for R&D for novel antibioticsDrug Resist UpdateYear: 2011148994
Salerno F,Cazzaniga M,Therapeutic strategies and emergence of multiresistant bacterial strainsIntern Emerg MedYear: 20105455110.1007/s11739-010-0447-9
Zhao Y,Tian Y,Cui Y,Liu W,Ma W,Jiang J,Small molecule-capped gold nanoparticles as potent antibacterial agents that target gram-negative bacteriaJ Am Chem SocYear: 2010132123491235610.1021/ja102884320707350
Balland O,Pinto-Alphandary H,Viron A,Puvion E,Andremont A,Couvreur P,Intracellular distribution of ampicillin in murine macrophages infected with Salmonella typhimurium and treated with (3H) ampicillin-loaded nanoparticlesJ Antimicrob ChemotherYear: 1996371051158647751
Rosemary MJ,MacLaren I,Pradeep T,Investigations of the antibacterial properties of ciprofloxacin@SiO2LangmuirYear: 200622101251012910.1021/la061411h17107009
Rosi NL,Giljohann DA,Thaxton CS,Lytton-Jean AK,Han MS,Mirkin CA,Oligonucleotide-modified gold nanoparticles for intracellular gene regulationScienceYear: 20063121027103010.1126/science.112555916709779
Thomas M,Klibanov AM,Conjugation to gold nanoparticles enhances polyethylenimine’s transfer of plasmid DNA into mammalian cellsProc Natl Acad Sci USAYear: 20031009138914310.1073/pnas.123363410012886020
Cho EC,Au L,Zhang Q,Xia Y,The effects of size, shape, and surface functional group of gold nanostructures on their adsorption and internalization by cellsSmallYear: 2010651752210.1002/smll.20090162220029850
Bowman MC,Ballard TE,Ackerson CJ,Feldheim DL,Margolis DM,Melander C,Inhibition of HIV fusion with multivalent gold nanoparticlesJ Am Chem SocYear: 20081306896689710.1021/ja710321g18473457
Gu H,Ho PL,Tong E,Wang L,Xu B,Using biofunctional magnetic nanoparticles to capture vancomycin-resistant Enterococci and other gram-positive bacteria at ultralow concentrationNano LettYear: 200331261126310.1021/nl034396z
Buzea C,Pacheo I,Robbie K,Nanomaterials and nanoparticles: sources and toxicityBiointerphasesYear: 2007228156902815745
Nair LS,Laurencin CT,Role of size scale of ZnO nanoparticles and microparticles on toxicity towards bacteria and osteoblast cancer cellsJ Biomed NanotechnolYear: 2007330131610.1166/jbn.2007.041
Reddy KM,Feris K,Bell J,Wingett DG,Hanley C,Punnoose A,Selective toxicity of zinc oxide nanoparticles to prokaryotic and eukaryotic systemsAppl Phy LettYear: 20079021390210.1063/1.2742324
Jeng HA,Swanson J,Toxicity of metal oxide nanoparticles in mammalian cellsJ Enviorn Sci HealthYear: 2006412699
Ruparelia JP,Chatterjee AK,Duttagupta SP,Mukherji S,Strain specificity in antimicrobial activity of silver and copper nanoparticlesActa BiomaterYear: 2008470771610.1016/j.actbio.2007.11.00618248860
Prabhu BM,Ali SF,Murdock RC,Hussain SM,Srivatsan M,Copper nanoparticles exert size and concentration dependent toxicity on somatosensory neurons of ratNanotoxicologyYear: 2010415016010.3109/1743539090333769320543894
Morones JR,Elechiguerra JL,Camacho A,Holt K,Kouri JB,Ramirez JT,Yacaman M,The bactericidal effect of silver nanoparticlesJYear: 2005162346235310.1088/0957-4484/16/10/059
Ahamed M,Karns M,Goodson M,Rowe J,Hussain SM,Schlager JJ,Hong Y,DNA damage response to different surface chemistry of silver nanoparticles in mammalian cellsToxicol Appl PharmacolYear: 200823340441010.1016/j.taap.2008.09.01518930072
Norman RS,Stone JW,Gole A,Murphy CJ,Sabo ATL,Targeted photothermal lysis of the pathogenic bacteria, Pseudomonas aeruginosa, by gold nanorodsNano LettYear: 2008830230610.1021/nl072705618062714
Panyala N,Pena-Mendze E,Havel J,Silver or silver nanoparticles: a hazardous threat to the environment and human health?Jour of App BiomedYear: 20086117129
Love JC,Estroff LA,Kriebel JK,Nuzzo RG,Whitesides GM,Self-assembled monolayers of thiolates on metals as a form of nanotechnologyChem RevYear: 20051051103117010.1021/cr030078915826011
Cheng CMM,Cuda G,Bunimovich LY,Gaspari M,Heath RJ,Hill DH,Mirkin AC,Nijdam JA,Terracciano R,Thundat T,Ferrari M,Nanotechnologies for biomolecular detection and medical diagnosticsCurr Opin Chem BiolYear: 200610111910.1016/j.cbpa.2006.01.00616418011
Hu M,Chen J,Li ZY,Au L,Hartland GV,Li X,Marqueze M,Xia Y,Gold nanostructures: engineering their plasmonic properties for biomedical applicationsChem Soc RevYear: 2006351084109410.1039/b517615h17057837
Shim SY,Lim DK,Nam JM,Ultrasensitive optical biodiagnostic methods using metallic nanoparticlesNanomedicineYear: 2008321523210.2217/17435889.3.2.21518373427
Huang WC,Tsai PJ,Chen YC,Functional gold nanoparticles as photothermal agents for selective-killing of pathogenic bacteriaNanomedicineYear: 2007277778710.2217/17435889.2.6.77718095845
Kovtun A,Heumann R,Epple M,Calcium phosphate nanoparticles for the transfection of cellsBiomed Mater EngYear: 20091924124719581719
Bunz UH,Rotello VM,Gold nanoparticle-fluorophore complexes: sensitive and discerning “noses” for biosystems sensingAngew Chem Int Ed EnglYear: 2010493268327910.1002/anie.20090692820405519
Wu W,Li AD,Research focus: optically switchable nanoparticles for biological imagingNanomedicineYear: 2007252353110.2217/17435889.2.4.52317716135
Liao HW,Nehl CL,Hafner JH,Biomedical applications of plasmon resonant metal nanoparticlesNanomedicineYear: 2006120120810.2217/17435889.1.2.20117716109
Erathodiyil N,Ying JY,Functionalization of inorganic nanoparticles for bioimaging applicationsAcc Chem ResYear: 20114492593510.1021/ar200032721648430
Kelly LK,Coronado E,Zhao L,Schatz GC,The optical properties of metal nanoparticles: the influence of size, shape, and dielectric environmentJ Phys Chem BYear: 2003107668677
Auffan M,Bottero YJ,Chaneac C,Rose J,Inorganic manufactured nanoparticles: how their physicochemical properties influence their biological effects in aqueous environmentsNanomedicineYear: 20105999100710.2217/nnm.10.6120735233
Pal S,Yu KT,Song M,Does the antibacterial activity of silver nanoparticles depend on the shape of the nanoparticle? A study of the gram-negative bacterium Escherichia coliJ Appl Environ MicrobiolYear: 2007731712172010.1128/AEM.02218-06
Badwaik DV,Bartonojo JJ,Evans WJ,Sahi VS,Willis BC,Dakshinamurthy R,Single-step bio-friendly synthesis of surface modifiable, near-spherical gold nanoparticles for applications in biological detection and catalysisLangmuirYear: 2011275549555410.1021/la105041d21480600
Robert DS,Robert LH,Martha V,Benedict’s solution, a reagent for measuring reducing sugars: the clinical chemistry of Stanley RBenedict J Biol ChemYear: 19085485487
Vernon LP,Edward SW,The volumetric estimation of hydroxyl groups in sugars and other organic compoundsJ Biol ChemYear: 192774379383
Daniel MC,Ruiz J,Nlates S,Blais JC,Astrus D,Nanoscopic assemblies between supramolecular redox active metallodendrons and gold nanoparticles: synthesis, characterization, and selective recognition of H2PO4−, HSO4−, and adenosine-5′-triphosphate (ATP2−) anionsJ Am Chem SocYear: 20031252617262810.1021/ja021325d12603150
Leff DV,Ohara PC,Heath JR,Gelbart WM,Crystallization of opals from polydisperse nanoparticlesJ Phys ChemYear: 1995997036704110.1021/j100018a041
Chamundeeswari M,Sobhana LSS,Jacob PJ,Kumar GM,Devi PM,Sastry PT,Mandal BA,Preparation, characterization and evaluation of a biopolymeric gold nanocomposite with antimicrobial activityBiotechnol Appl BiochemYear: 201055293510.1042/BA2009019819929854
Burygin LG,Khlebtsov NB,Shantrokha NA,Dykman AL,Bogatyrev AV,Khlebtsov GN,On the enhanced antibacterial activity of antibiotics mixed with gold nanoparticlesNanoscale Res LettYear: 2009479480110.1007/s11671-009-9316-820596384
Shrivastava S,Bera T,Roy A,Singh G,Ramachandrarao P,Dash D,Characterization of enhanced antibacterial effects of novel silver nanoparticlesNanotechnologyYear: 20071822510322511210.1088/0957-4484/18/22/225103
Santhana RL,Hing HL,Baharudin O,Teh HZ,Aida SR,Nor ACP,Vimala B,Paramsarvaran S,Sumarani G,Hanjeet K,Rapid method for transmission electron microscope study of Staphylococcus aureus ATCC 25923Ann MicroscopeYear: 20077102108
Jung KW,Koo CH,Kim WK,Shin S,Kim HS,Park HY,Antibacterial activity and mechanism of action of the silver ion in Staphylococcus aureus and Escherichia coliAppl Environ MicrobiolYear: 2008742171217810.1128/AEM.02001-0718245232
Kadurugamuwa JL,Clarke AJ,Beveridge TJ,Surface action of gentamicin on Pseudomonas aeruginosaJ BacteriologyYear: 199317557985805
Vaara M,Agents that increase the permeability of the outer membraneMicrobiol RevYear: 1992563954111406489
Lowy DF,Staphylococcus aureus infectionsN Engl J MedYear: 199833952053210.1056/NEJM1998082033908069709046
Ryan KJ,Ray CG,An introduction to infectious diseasesMedical MicrobiologyYear: 20044345347
Ndeke M,Melusi T,Nomakhwezi N,The antibacterial effects of engineered nanomaterials: implications for wastewater treatment plantsJ Enviorn MonitorYear: 2011131164118310.1039/c1em10023h

Figures

[Figure ID: F1]
Figure 1 

Effect of different sizes of dextrose-encapsulated GNPs on the growth of E. coli. Growth analysis curves were measured by monitoring the optical density (OD) at 600 nm, and the E. coli was treated with dGNPs of sizes: 25 ± 5; 60 ± 5. and 120 ± 5 nm at different concentrations (NPs/mL).



[Figure ID: F2]
Figure 2 

Plate assay showing the number of viable cells recovered after treatment of E. coli with dGNPs. (A) The bacterial cells were treated with dGNPs in the liquid media for 12 h and then were spread on the agar plates and incubated for further 12 h. (B) Plot of the number of E. coli colonies recovered against the number of dGNPs.



[Figure ID: F3]
Figure 3 

Visualization of dGNP induced morphological changes in E. coli cell membranes under the TEM. (A) Morphology of the untreated E. coli cell at 0 h (a); cross section of the untreated E. coli cell after 12 h (b). (B) Interaction of dGNPs with E. coli cell at 0 h (a); cross section of the dGNPs treated E. coli cell after 6 h showing the initiation of the cell disruption by the formation of outer membrane vesicles (OMVs) (b); cross section of the lysed E. coli cell after 12 h of treatment with dGNPs (c); the magnified view of OMV formation, which represents the initiation of disruption of cell membrane (d).



[Figure ID: F4]
Figure 4 

Monitoring dGNPs-induced permeability of E. coli cell membranes and leakage of nucleic acids. (A) The left half shows an image in the differential interference contrast mode, while the right half shows the corresponding fluorescence image. (B) The percentage of cells with permeable membranes from five or more fields of view obtained by two independent experiments.



[Figure ID: F5]
Figure 5 

Spread plate assays of S. epidermidis after treatment with dGNPs at different concentrations. (A) Plate assay showing the number of viable cells recovered after the treatment of S. epidermidis without (control) or with dGNPs). (B) Graphs plotted for the number of S. epidermidis colonies recovered against the number of dGNPs.



[Figure ID: F6]
Figure 6 

Visualizing dGNP-induced morphological changes of S. epidermidis cell membranes via TEM. (A) Morphology of the untreated S. epidermidis cells at 0 h (a); cross section of the untreated S. epidermidis cell after 12 h (b). (B) Interaction of dGNPs with S. epidermidis cell at 0 h (a); cross section of the dGNPs-treated S. epidermidis cell after 6 h showing the initiation of the cell wall disruption (b); cross section of the lysed S. epidermidis cell after 12 h of treatment with dGNPs (c).



[Figure ID: F7]
Figure 7 

Monitoring of dGNPs-induced permeability of S. epidermidis cell membranes via propidium iodide. (A) For each image the left half shows an image in the differential interference contrast mode, while the right half shows the corresponding fluorescence image. (B) The percentage of cells with permeable membranes from five or more fields of view obtained by two independent experiments.



Article Categories:
  • Nano Express

Keywords: Gold nanoparticles, Green synthesis, Antibacterial activity, Propidium iodide, Outer membrane vesicles.

Previous Document:  Accuracy of pedigree and genomic predictions of carcass and novel meat quality traits in multi-breed...
Next Document:  On the HORYZON: Moderated online social therapy for long-term recovery in first episode psychosis.