Single-step route to diamond-nanotube composite.
Jump to Full Text
MedLine Citation:
PMID:  23013660     Owner:  NLM     Status:  PubMed-not-MEDLINE    
Abstract/OtherAbstract:
Candle wax was used as a precursor for the production of a diamond-nanotube composite in a single step. The composite films were fabricated by sulfur-assisted hot-filament chemical vapor deposition technique. The morphology of the composite films was analyzed by scanning electron microscopy and transmission electron microscopy. Raman spectra of the films show characteristic diamond band at 1,332 cm-1, D-band around 1,342 cm-1, and graphitic G-band around 1,582 cm-1. The electron energy-loss spectroscopy recorded at the carbon K-edge region shows signature features of diamond and carbon nanotube in the fabricated material. The ability to synthesize diamond-nanotube composites at relatively low temperatures by a single-step process opens up new possibilities for the fabrication of nanoelectronic devices.
Authors:
Deepak Varshney; Majid Ahmadi; Maxime J-F Guinel; Brad R Weiner; Gerardo Morell
Publication Detail:
Type:  Journal Article     Date:  2012-09-27
Journal Detail:
Title:  Nanoscale research letters     Volume:  7     ISSN:  1556-276X     ISO Abbreviation:  Nanoscale Res Lett     Publication Date:  2012  
Date Detail:
Created Date:  2012-12-12     Completed Date:  2012-12-13     Revised Date:  2013-03-13    
Medline Journal Info:
Nlm Unique ID:  101279750     Medline TA:  Nanoscale Res Lett     Country:  United States    
Other Details:
Languages:  eng     Pagination:  535     Citation Subset:  -    
Affiliation:
Department of Physics, University of Puerto Rico, San Juan, PR, 00936-8377, USA. deepvar20@gmail.com.
Export Citation:
APA/MLA Format     Download EndNote     Download BibTex
MeSH Terms
Descriptor/Qualifier:
Comments/Corrections

From MEDLINE®/PubMed®, a database of the U.S. National Library of Medicine

Full Text
Journal Information
Journal ID (nlm-ta): Nanoscale Res Lett
Journal ID (iso-abbrev): Nanoscale Res Lett
ISSN: 1931-7573
ISSN: 1556-276X
Publisher: Springer
Article Information
Download PDF
Copyright ©2012 Varshney et al.; licensee Springer.
open-access:
Received Day: 19 Month: 7 Year: 2012
Accepted Day: 18 Month: 9 Year: 2012
collection publication date: Year: 2012
Electronic publication date: Day: 27 Month: 9 Year: 2012
Volume: 7 Issue: 1
First Page: 535 Last Page: 535
PubMed Id: 23013660
ID: 3519742
Publisher Id: 1556-276X-7-535
DOI: 10.1186/1556-276X-7-535

Single-step route to diamond-nanotube composite
Deepak Varshney12 Email: deepvar20@gmail.com
Majid Ahmadi1 Email: mjd_ahmadi@yahoo.com
Maxime J-F Guinel123 Email: maxime.guinel@upr.edu
Brad R Weiner23 Email: brad@hpcf.upr.edu
Gerardo Morell12 Email: gerardo.morell@upr.edu
1Department of Physics, University of Puerto Rico, San Juan, PR, 00936-8377, USA
2Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR, 00931-3334, USA
3Department of Chemistry, University of Puerto Rico, San Juan, PR, 00936-8377, USA

Background

Since the documented discovery of carbon nanotubes (CNTs) in 1991 by Iijima [1] and the realization of their unique physical properties, including mechanical, thermal, and electrical, many investigators have endeavored to fabricate advanced CNT composite materials that exhibit one or more of these properties. Integration of CNTs with various kinds of materials, leading to the fabrication of composites possessing properties of the individual components with a synergistic effect, has gained growing interest. Carbon composites, such as diamond-nanotube, have various industrial applications because of their outstanding physical and chemical properties. CNTs are tiny rolled-up tubes of sp2-hybridized carbon that possess unique electronic transport properties and are the strongest known material, while diamond, consisting of sp3-hybridized carbon, exhibits high hardness, stable surface chemistry, and good biocompatibility [2,3]. The exceptional mechanical and electronic properties of CNTs and diamond make them promising candidates for use in microelectronic devices. A diamond-nanotube composite has excellent thermal conductivity and field emission characteristics and finds applications in various fields that require a combination of good thermal and electrical properties such as wear-resistant coatings, thermal management of integrated circuits, field emission devices, and electrical field shielding in MEMS and microelectronics [4].

There are several recent reports on the development of hybrid materials comprising of diamond and CNTs [4-6]. However, the reported methods have either two distinct seeding sources or a tedious two-step fabrication route which requires the use of a catalyst to provide initial nucleation sites for growth of both CNTs and diamond. To enhance the nucleation rate during diamond film growth, various techniques such as ultrasonic seeding [7], surface scratching, and bias-enhanced nucleation have been applied [8,9]. All the above techniques are mechanically abrasive and adversely affect the use of substrate for electronic applications, thus fueling the need for precursors that are cheap and handy and do not harm the substrate surface. Also, the transition metal catalysts, viz. Fe, Co, and Ni, that are used for CNT growth [10-12] react unfavorably with materials found in circuits and composites. Moreover, catalyst nanopowder can be toxic and cause problems in clean room environments. The present paper reports the catalyst-free growth of CNTs that is seeded by paraffin wax.

There are many reports on the fabrication of single-walled carbon nanotubes from polymers using metal catalyst [13,14]. In all previously reported techniques, the hybrid material was fabricated in two separate steps, each for metal-catalyzed CNT growth and diamond nanoparticle seeded diamond growth, but a single-step fabrication of diamond-nanotube composite using a single seeding source has been difficult. Here, we report the fabrication of diamond-nanotube composite by hot-filament chemical vapor deposition (HFCVD) in a single-step process, where paraffin wax is utilized as a seeding material for both diamond and carbon nanotubes. In the present report, trace amounts of sulfur have been used in the fabrication process to aid the formation of CNTs. The role of sulfur is explained in the ‘Results and discussion’ section. This paper demonstrates a new synthetic pathway for diamond-nanotube composite utilizing candle wax (paraffin wax), a cheap and widely used hydrocarbon.


Methods

Polycrystalline copper substrates (99.9% pure, 0.5-mm thick, and 14-mm disk diameter) were hand polished with 600-grit sandpaper on both sides to make them flat. One side was further polished with 1,000-, 1,500-, and 2,000-grit sandpaper to smoothen the surface. The substrates were then cleaned in an ultrasonic bath with 2-propanol for 15 min and then dried with nitrogen. About 5 to 10 gm of candle wax (commercially available) was melted on a hot plate in a glass beaker by heating it to a temperature of 120°C at a rate of 15°C/min. A small portion of this melt was transferred onto a copper disk substrate with a thickness of 500 to 700 nm and allowed to cool to room temperature. The disks were then placed in the HFCVD chamber and exposed to a gas mixture of 0.3% methane and 99.7% of hydrogen (consisting of 500 ppm of H2S) at a constant pressure of 20 Torr and a total gas flow of 100 sccm. The reaction was activated for 3 h by a rhenium filament (8 cm in length and 0.5 mm in diameter) positioned 8 mm above the substrate. The temperature of the substrate and the filament was at approximately 550°C and 2,500°C, respectively.

The Raman scattering spectra were obtained using a triple monochromator (ISAJ-Y Model T 64000, HORIBA Ltd., Kyoto, Japan) with around 1 cm−1 resolution using the 514.5-nm line of Ar laser. The morphologies of the as-deposited materials were determined using a JEOL JEM-7500 F scanning electron microscope (SEM; JEOL Ltd., Tokyo, Japan).

The samples were also analyzed using a Carl Zeiss LEO 922 energy-filtered transmission electron microscope (TEM; Carl Zeiss AG, Oberkochen, Germany) operated at 200 kV, including an omega-type energy filter to study the electron energy-loss spectroscopy (EELS). The TEM samples were prepared by immersing an ultrathin carbon-coated copper grid into an ultrasonicated suspension of the fabricated material in ethanol. The Fourier transform infrared spectroscopy (FTIR) was carried out using a Bruker Tensor 27 instrument (Bruker Optik GmbH, Ettlingen, Germany). The samples were prepared by melting 0.5 g of wax onto the substrate and allowing it to cool to room temperature.


Results and discussion

Candle wax is generally composed of paraffin, which is made of heavy straight-chain hydrocarbons obtained from crude petroleum oil [15]. Crystalline paraffin waxes are solid and crystalline mixtures of hydrocarbons consisting of linear n-alkane and branched iso- and cyclo-alkanes with carbon lengths ranging from C16 to C30 and higher [16,17]. The paraffin crystallites seem to act as nucleation sites for diamond and carbon nanotube growth in the presence of hydrocarbon radicals and atomic hydrogen in the chemical vapor deposition (CVD) system, resulting in microcrystalline diamond-carbon nanotube films [18].

The morphology of the diamond-nanotube composite films was ascertained by SEM. Figure 1a,b,c reveals a network of carbon nanotubes entangling the diamond microcrystals. The microcrystals with size ranging from 0.4 to 1.0 μm are randomly nucleated in a web of several-microns-long carbon nanotubes. From the SEM images (Figure 1a,b,c), we notice that the distribution of the diamond microcrystals and the nanotubes on the substrate has a bimodal distribution, which implies that the diamond crystals and nanotubes have been fabricated in a single step.

FTIR spectroscopy was used to analyze the chemical composition of paraffin wax, and the obtained spectrum is shown in Figure 2, which reveals the presence of carbon-hydrogen stretching and bending absorption bands in the range of 1,000 to 3,000 cm−1. The symmetric carbon-hydrogen bending absorption of the CH3 group at 1,380 cm−1, the CH deformation around 1,460 cm−1, and the CH2 rocking absorption band at 725 cm−1 confirm the linear saturated aliphatic structure of the paraffin wax [19]. The FTIR spectrum of the paraffin melt does not contain any bands for oxygen, confirming the absence of oxygen in the paraffin melt.

The Raman spectra of the wax-coated substrate (Figure 3) show the typical vibrational modes of paraffin, which is the most common polymer in industrial and everyday household use. The characteristic fundamental vibrational modes observed between 1,000 and 2,000 cm−1 are frequently used to study morphological structure. The spectra show distinctive Raman contributions at 1,063, 1,133, 1,171, 1,296, 1,418, 1,441, and 1,463 cm−1 that are attributed to C-C (carbon-carbon) stretching and the CH2 and CH3 deformations [20] which arise from the straight-chain hydrocarbon structure of the seeding polymer [21]. Figure 3 shows the Raman spectrum of the composite film revealing a sharp and intense peak at 1,332.6 cm−1, which is the signature of sp3-bonded C in diamond phase [22]. The shoulder around 1,350 cm−1 corresponds to the disorder induced in the sp2 carbon [23]. The band at about 1,603 cm−1 corresponds to sp2-hybridized carbon, indicating the presence of graphitic carbon [24]. The absence of typical vibrational modes of candle wax confirms that it acts as a seeding source for diamond and also for CNTs. We propose a phenomenological explanation of the synthesis of diamond-nanotube composite from a single seeding source (candle wax).

The genesis of diamond-nanotube composite from candle wax seeds can be understood qualitatively through a mechanism (Figure 4) based on the current understanding of the CVD of diamond and CNTs and the decomposition of candle wax. Candle wax consists of long chains of n-alkanes with melting point in the range of 58°C to 62°C and a flash point starting at 204°C. Under HFCVD conditions above the flash point, the candle wax decomposes, leaving behind sp2-C and sp3-C crystallites [22,25] on the Cu substrate surface, which act as nuclei for the CNTs and diamond, respectively. Another factor that influences the crystal formation is the interactive forces on the surface [26]. Any non-carbide-forming substrate, such as Cu, Ag, or Au, provides a surface with minimal surface interactions, thus facilitating the formation of sp2-C and sp3-C crystallites. Under typical HFCVD conditions, atomic H etches away the sp2-C crystallites, thus favoring the formation of microcrystalline diamond. However, the addition of trace amounts of sulfur, in the form of hydrogen sulfide, to the chemical vapor deposition reaction leads to profound changes in the gas phase chemistry and the surface chemistry. The high temperature around the filament leads to the dissociation of H2S and CH4 to form SH radicals along with carbon radicals. When the radicals move away from the filament to a cooler region at the substrate surface, the active SH radicals combine with C radicals to form CS radicals, which combine with hydrogen atoms to form H2S again while depositing carbon atoms onto the substrate surface [27]. The net effect is analogous to hydrogen depletion, thus avoiding the preferential etching of sp2-C crystallites. These conditions promote the growth of CNTs by surface diffusion of carbon, leading to a CNT growth mechanism known as the ‘vapor-solid surface-solid’ mechanism [28]. Simultaneously, the sp3-C crystallites grow into diamond microcrystals through the usual mechanism. In essence, the presence of sulfur increases the CNT growth rate, making it more rapid than the etching rate of CNTs in the presence of atomic hydrogen. These results open new possibilities for diamond and carbon nanotubes to be grown simultaneously using a cheap seeding source without the use of a metal catalyst.

TEM studies were used for further characterization of the diamond-nanotube composite films. Figure 5 shows the TEM images of the carbon nanotubes and diamond particles. Figure 5a shows diamond crystals with size ranging from 350 to 450 nm together with carbon nanotubes. The inset of Figure 5a shows selected area electron diffraction pattern recorded from the microcrystalline diamond. The polycrystalline diffraction rings correspond to {111}, {220}, and {311} and are in agreement with the diamond lattice structure. Figure 5b shows the TEM image of the composite film revealing the presence of carbon nanotubes. The inset of Figure 5b shows the magnified image of carbon nanotubes, which were found to have a diameter in the range of 40 to 50 nm.

EELS were recorded in the carbon K-edge region near-edge structure between 285 to 310 eV and was used to investigate the structure of the composite film (shown in Figure 6). EELS were recorded on different regions of the composite film, which are shown in Figure 5a and are indicated by arrows. The EELS spectrum of the tubular structure (black line) shows edge around 285 eV due to 1s to low-lying antibonding π* transitions and around 292 eV due to the 1s to σ* transition. The energy-loss spectrum recorded from the diamond particles (blue line) clearly shows the presence of a dip around 301 eV due to the second absolute bandgap of diamond [29], which distinguishes it from carbon nanotubes.


Conclusions

A simple and reproducible single-step method for the fabrication of diamond-nanotube composite films was reported. The characteristic features of both carbon nanotubes and diamond in the composite film were evident from the Raman spectroscopy, EELS, SEM, and TEM results. To our knowledge, this is the first example of a sulfur-based growth of diamond-nanotube composite. The low-temperature fabrication of the present diamond-nanotube composite without the use of a metal catalyst and in a single-step process opens up new possibilities for the fabrication of composite-based nanoelectronic devices.


Competing interests

The authors declare that they have no competing interests.


Authors’ contributions

DV synthesized and characterized the hybrid films and wrote the manuscript. MA and MJFG did the SEM and TEM analyses. BRW and GM supervised the study. All authors read and approved the final manuscript.


Authors’ information

DV and MA are PhD students at the University of Puerto Rico (UPR). MJFG is an assistant professor at the Department of Physics and Department of Chemistry at UPR. BRW is a dean and professor at UPR. GM is a professor and the director of the Department of Physics at UPR.


Acknowledgments

This research project was carried out under the auspices of the Institute for Functional Nanomaterials (NSF grant no. 1002410). This research was also supported in part by PR NASA EPSCoR (NNX07AO30A) and PR NASA Space Grant (NNX10AM80H). The authors gratefully acknowledge the instrumentation and technical support of the Raman Facility (Dr. R.S. Katiyar).


References
Iijima S,Helical microtubules of graphitic carbonNatureYear: 1991354565810.1038/354056a0
Singh SV,Zaharia T,Creatore M,Groenen R,Van Hege K,Van de Sanden MCM,Hard graphite like hydrogenated amorphous carbon grown at high rates by a remote plasmaJ App PhysYear: 201010701330501331410.1063/1.3273412
Tang L,Tsai C,Gerberich WW,Kruckeberg L,Kania DR,Biocompatibility of chemical-vapour-deposited diamondBiomaterYear: 19951648348810.1016/0142-9612(95)98822-V
Xiao X,Elam JW,Trasobares S,Auciello O,Carlisle JA,Synthesis of a self assembled hybrid of ultrananocrystalline diamond and carbon nanotubesAdv MaterYear: 200517149610.1002/adma.200401581
Terranova M,Orlanducci S,Fiori A,Tamburi E,Sessa V,Rossi M,Barnard A,Controlled evolution of carbon nanotubes coated by nanodiamond: the realization of a new class of hybrid nanomaterialsChem MaterYear: 200517321410.1021/cm0502018
Gruen DM,Liu S,Krauss AR,Luo J,Pan X,Fullerenes as precursors for diamond film growth without hydrogen or oxygen additionsApp Phys LettYear: 1994641502150410.1063/1.111872
Williams OA,Douhe'ret O,Daenen M,Haenen K,Osawa E,Takahashi M,Enhanced diamond nucleation on monodispersed nanocrystalline diamondChem Phys LettYear: 200744525525810.1016/j.cplett.2007.07.091
Arnault JC,Saada S,Delclos S,Intiso L,Tranchant N,Polini R,Bergonzo P,In situ study of the initial stages of diamond deposition on 3C–SiC (100) surfaces: towards the mechanisms of diamond nucleationDiam Relat MaterYear: 20071669069410.1016/j.diamond.2006.12.036
Sumant AV,Gilbert PUPA,Grierson DS,Konicek AR,Abrecht M,Butler JE,Feygelson T,Rotter SS,Carpick RW,Surface composition, bonding, and morphology in the nucleation and growth of ultra-thin, high quality nanocrystalline diamond filmsDiam Relat MaterYear: 20071671872410.1016/j.diamond.2006.12.011
Maruyama S,Kojima R,Miyauchi Y,Chiashi S,Kohno M,Low-temperature synthesis of high-purity single-walled carbon nanotubes from alcoholChem Phys LettYear: 200236022923410.1016/S0009-2614(02)00838-2
Taniguchi M,Nagao H,Hiramatsu M,Ando Y,Hori M,Preparation of dense carbon nanotube film using microwave plasma-enhanced chemical vapor depositionDiam Relat MaterYear: 20051485585810.1016/j.diamond.2004.10.002
Liu JW,Wang X,Zheng WT,Li JX,Guan QF,Su YD,Qi JL,Jiang Q,Alignment of amorphous carbon nanotubes with graphitized branches grown by radio frequency plasma-enhanced chemical vapor depositionCarbonYear: 20074568168410.1016/j.carbon.2006.11.026
Kumar M,Ando Y,Carbon nanotubes from camphor: an environment-friendly nanotechnologyJ Phys: Conf SeriesYear: 200761643646
Puengjinda P,Sano N,Tanthapanichakoon W,Charinpanitkul T,Selective synthesis of carbon nanotubes and nanocapsules using naphthalene pyrolysis assisted with ferroceneJ Ind Eng ChemYear: 200915337538010.1016/j.jiec.2008.11.003
Saber O,Hefny N,Al Jaafari AA,Improvement of physical characteristics of petroleum waxes by using nano-structured materialsFuel J Process TechnolYear: 20119294695110.1016/j.fuproc.2010.12.015
Kuszlik AK,Meyer G,Heezen PAM,Stepanski M,Solvent-free slack wax de-oiling-physical limitsJ Chem Eng Res DYear: 2010881279128310.1016/j.cherd.2010.01.009
Zaky MT,Mohamed NH,Comparative study on separation and characterization of high melting point macro- and micro-crystalline waxesJ Taiw Inst Chem EngYear: 20104136036610.1016/j.jtice.2009.09.003
Varshney D,Makarov VI,Saxena P,Guinel MJ-F,Kumar A,Scott JF,Weiner BR,Morell G,Electron emission from diamond films seeded using kitchen-wrap polyethyleneJ Phys D: Appl PhysYear: 201144085502. 7
Cho SY,Fogle HS,Efforts on solving theproblem of paraffin deposit. I: using oil-soluble inhibitorsJ Ind Eng ChemYear: 199952123127
Zheng M,Du W,Phase behavior, conformations, thermodynamicproperties, and molecular motionof multicomponent paraffin waxes. A Raman spectroscopy studyVib SpectroscYear: 20064021910.1016/j.vibspec.2005.10.001
Faoláin EÓ,Hunter MB,Byrne JM,Kelehan P,Lambkin HA,Byrne HJ,Lyng FM,Raman spectroscopic evaluation of efficacy of current paraffin wax section dewaxing agentsJ Histochem CytochemYear: 20055312115637345
Field JE,The properties of diamondYear: 1979Academic Press, London
Kalss W,Haubner R,Lippold G,Lux B,Diamond deposition on platinum and palladium-Raman investigationsDiam Relat MaterYear: 199872–5158164
Badzian AR,Badzian T,Roy R,Messier R,Spear KE,Crystallization of diamond crystals and films by microwave assisted CVDMater Res BullYear: 19882353154810.1016/0025-5408(88)90161-4
Edwards RT,Crystal habit of paraffin waxInd Chem Eng ChemYear: 195749475075710.1021/ie50568a042
Wang RY,Rafailovich M,Sokolov J,Gersappe D,Araki T,Zou Y,Kilcoyne ADL,Ade H,Marom G,Lustiger A,Substrate effect on the melting temperature of thin polyethylene filmsPhys Rev LettYear: 20069602830316486656
Haubner R,Sommer D,Hot-filament diamond deposition with sulfur additionDiam Relat MaterYear: 2003123–7298305
Takagi D,Kobayashi Y,Homma Y,Carbon nanotube growth from diamondJ Am Chem SocYear: 20091316922692310.1021/ja901295j19405530
Varshney D,Kumar A,Guinel MJ-F,Weiner BR,Morell G,Spontaneously detaching self-standing diamond filmsDiam Relat MaterYear: 20122199102

Figures

[Figure ID: F1]
Figure 1 

SEM images of thediamond-nanotube composite film. (a) and (b) show diamond microcrystals entangled in a carbon nanotube network. (c) shows the diamond microcrystals with size ranging from 0.4 to 1.0 μm.



[Figure ID: F2]
Figure 2 

FTIR spectrum of theparaffin wax melt. It confirms the absence of oxygen in the paraffin melt.



[Figure ID: F3]
Figure 3 

Raman spectrum of thediamond-nanotube composite film. The spectrum shows bands corresponding to the presence of diamond and carbon nanotubes in the composite film.



[Figure ID: F4]
Figure 4 

Schematic representation of themechanism of diamond-nanotube compositefilm formation. Formation of diamond-nanotube composite having diamond crystals (gray in color) entangled in the carbon nanotubes (black lines).



[Figure ID: F5]
Figure 5 

TEM images of thediamond-nanotube composite film. (a,b) TEM image showing the diamond microcrystals present in the diamond-nanotube composite film synthesized using paraffin wax. The inset of Figure 5a shows the corresponding electron diffraction pattern indexed to diamond with its {111}, {220} and {311} reflections. The inset of Figure 5b shows the magnified image of the carbon nanotubes.



[Figure ID: F6]
Figure 6 

EELS spectra of thediamond-nanotube composite film. The obtained spectra confirm the presence of carbon nanotubes and diamond microcrystals.



Article Categories:
  • Nano Express

Keywords: Carbon nanotubes, Diamond crystals, Chemical vapor deposition.

Previous Document:  Community incidence of pathogen-specific gastroenteritis: reconstructing the surveillance pyramid fo...
Next Document:  Clinical and diagnostic assessment for therapeutic decisions in prostate cancer.