Electrochemical Reduction of CO2 to Organic Acids by a Pd-MWNTs Gas-Diffusion Electrode in Aqueous Medium.
Jump to Full Text
MedLine Citation:
PMID:  24453849     Owner:  NLM     Status:  In-Data-Review    
Abstract/OtherAbstract:
Pd-multiwalled carbon nanotubes (Pd-MWNTs) catalysts for the conversion of CO2 to organic acids were prepared by the ethylene glycol reduction and fully characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), and cyclic voltammetry (CV) technologies. The amorphous Pd particles with an average size of 5.7 nm were highly dispersed on the surface of carbon nanotubes. Functional groups of the MWNTs played a key role in the palladium deposition. The results indicated that Pd-MWNTs could transform CO2 into organic acid with high catalytic activity and CO2 could take part in the reduction reaction directly. Additionally, the electrochemical reduction of CO2 was investigated by a diaphragm electrolysis device, using a Pd-MWNTs gas-diffusion electrode as a cathode and a Ti/RuO2 net as an anode. The main products in present system were formic acid and acetic acid identified by ion chromatograph. The selectivity of the products could be achieved by reaction conditions changing. The optimum faraday efficiencies of formic and acetic acids formed on the Pd-MWNTs gas-diffusion electrode at 4 V electrode voltages under 1 atm CO2 were 34.5% and 52.3%, respectively.
Authors:
Guang Lu; Hui Wang; Zhaoyong Bian; Xin Liu
Related Documents :
6500519 - Isolation of acid-resistant urinary trypsin inhibitors by high performance liquid chrom...
24077159 - Lipid-enhancement of activated sludges obtained from conventional activated sludge and ...
14694189 - Specificity determinants and diversification of the brassica self-incompatibility polle...
8580769 - Purification and characterisation of soluble invertases from leaves of arabidopsis thal...
24932669 - Forcefield_ncaa: ab initio charge parameters to aid in the discovery and design of ther...
2825769 - Partial purification and functional properties of an endoprotease from bovine neurosecr...
25420949 - Two new labdane diterpenoids from the rhizomes of isodon yuennanensis.
8061289 - Immunohistochemical evidence for coexistence of glycine and gaba in nerve terminals on ...
12608819 - Catalysis of the michael addition reaction by late transition metal complexes of binol-...
Publication Detail:
Type:  Journal Article     Date:  2013-12-22
Journal Detail:
Title:  TheScientificWorldJournal     Volume:  2013     ISSN:  1537-744X     ISO Abbreviation:  ScientificWorldJournal     Publication Date:  2013 Dec 
Date Detail:
Created Date:  2014-01-23     Completed Date:  -     Revised Date:  -    
Medline Journal Info:
Nlm Unique ID:  101131163     Medline TA:  ScientificWorldJournal     Country:  England    
Other Details:
Languages:  eng     Pagination:  424617     Citation Subset:  IM    
Export Citation:
APA/MLA Format     Download EndNote     Download BibTex
MeSH Terms
Descriptor/Qualifier:

From MEDLINE®/PubMed®, a database of the U.S. National Library of Medicine

Full Text
Journal Information
Journal ID (nlm-ta): ScientificWorldJournal
Journal ID (iso-abbrev): ScientificWorldJournal
Journal ID (publisher-id): TSWJ
ISSN: 1537-744X
Publisher: Hindawi Publishing Corporation
Article Information
Download PDF
Copyright © 2013 Guang Lu et al.
open-access:
Received Day: 5 Month: 8 Year: 2013
Accepted Day: 8 Month: 10 Year: 2013
collection publication date: Year: 2013
Electronic publication date: Day: 22 Month: 12 Year: 2013
Volume: 2013E-location ID: 424617
PubMed Id: 24453849
ID: 3885284
DOI: 10.1155/2013/424617

Electrochemical Reduction of CO2 to Organic Acids by a Pd-MWNTs Gas-Diffusion Electrode in Aqueous Medium
Guang Lu1
Hui Wang1* http://orcid.org/0000-0002-6299-4034
Zhaoyong Bian2
Xin Liu1
1College of Environmental Science and Engineering, Beijing Forestry University, Beijing 100083, China
2College of Water Sciences, Beijing Normal University, Beijing 100875, China
Correspondence: *Hui Wang: wanghui@bjfu.edu.cn
[other] Academic Editors: N. Ademollo, S. K. Akal Solmaz, and W. K. Jo

1. Introduction

Recently, the conversion of CO2 to useful fuels as a carbon source has attracted much attention due to its greenhouse effect and fossil shortage [1]. Many attempts have been made to reduce the accumulation of atmosphere CO2, such as carbon capture and sequestration (CCS) [2], chemical usage [3], photochemical reduction [4], and electrochemical reduction [5]. In particular, electrochemical reduction can not only decrease CO2 release but also produce a variety of valuable compounds with high current efficiency. The products such as formic acid, CO, methane, ethylene, methanol, and ethanol can further be used as feedstock for chemical industry [69]. In addition, the electric power can be supplied by solar, wind, and geothermal energy, which are regarded as renewable sources [10]. It can also replace a part of fossil fuel consumption, which can further decrease the CO2 emission [6].

The research on electrochemical reduction of CO2 was first reported in the 19th century and rose since the energy crisis in the 1970's [11, 12]. Gas-diffusion electrodes could be operated at high current density (200–600 mA/cm2), that is, 10 folds higher than those achieved using metal plate electrodes for CO2 reduction [13]. Meanwhile, it improves the gaseous reactants distribution over the surface of catalyst. Catalysts with the unique three-phase interface structure lead to the least mass transport resistance across the gas-liquid interface and to the high catalyst surface. Supporting materials used to fabricate gas-diffusion, electrodes are mainly carbon materials, such as carbon fiber [14], carbon paper [15], carbon nanotubes [1618], carbon clothes [19], and active carbon [20] owing to their resistance to acid/basic media, and possibility to control the porosity and surface chemistry within certain limits. Due to the nanometer size, low resistance, high surface area, chemical stability, special mechanical, and electronic properties, carbon nanotubes show excellent properties in microelectronics, composite materials, and electrical application. Hence, carbon nanotubes have been widely used for catalyst support as a suitable material [2123]. Additionally, metal loaded carbon nanotubes (NTs) have been investigated extensively for the catalysis. Nanoscale metal catalysts could be dispersed on the high area of supported NTs. In the meantime, the interaction of carbon nanotubes with gas adsorbed either on or inside the tube or between aggregated MWNT attracts increasing attention due to the possible influence of the adsorption on some of the tubes properties and to the possibility of using these materials for efficient gas storage [24]. High concentrations of gas adsorbed by MWNTs can give rise to high-pressure-like effects at ambient pressures and promote the reduction by changing the reaction equilibrium. But until now, no sufficient investigation has been made on electrochemical reduction of CO2 on gas-diffusion electrode, using CNTs as support materials.

In this paper, Pd nanoparticle was decorated on MWNTs by ethylene glycol reduction. The prepared catalyst was then fabricated to the gas-diffusion cathode. The reduction of CO2 was performed in a cell with an organic synthetic diaphragm, a Ti/RuO2 anode, and self-made gas-diffusion cathode. On the base of catalyst and gas-diffusion electrode characterization, the key parameters of CO2 conversion were studied. Finally, the selectivity and efficiency of the formed products in the present and control systems were investigated.


2. Materials and Methods
2.1. Preparation of Pd-MWNTs Catalyst and Gas-Diffusion Cathode

The modifications of MWNTs (Shenzhen Nanotech Port Co. Ltd) were performed by heating 1.5 g MWNTs with 50 mL mixed concentrated acids (H2SO4-HNO3 mixture, 3 : 1 v/v ratio) for 1 h at 60°C. The product was filtered and washed with distilled water till neutrality. Then the solid was dried for 12 h at 70°C. Additionally 1.7 mg palladium chloride was dissolved in 15 mL ethylene glycol (reducing agent) with 13.6 mg sodium citrate to prevent the glomeration of palladium. After vigorously stirring for half an hour, ethylene glycol that contains 5% NaOH was added drop wise in order to maintain min pH at 10. Finally, treated MWNTs with the 100 : 1 mass ratio to palladium were added into the solution. After ultrasonic processing for 10 min, the vigorously stirred mixture was heated at 140°C. pH was kept above 10 by adding sodium hydroxide solution. The reaction was not over until the pH was constant. The mixture was then cooled down at room temperature, and filtered until no Cl was detected in filtrate. Remained solid was kept at 70°C for 12 h. Pd-MWNTs with a Pd load of 1 wt% were obtained. Gas diffusion layer was made of MWNTs. The gas-diffusion electrodes were made according to previous report [25]. It was made up of three parts: catalyst layer, gas-diffusion layer, and a stainless steel mesh. The catalyst layer was prepared with a mixture of 1.2 g 1 wt% Pd/MWNTs, 5.0 mL ethanol as a dispersant, and 3 g 10% PTFE as a wet-proofing agent and blinder. Beat and mix the mixture at 80°C until it emerged as a thin catalysts layer (5 cm × 6 cm, 0.4 mm thick). The gas-diffusion layer was prepared according to the procedure for making the catalyst layer except a mixture of 0.75 g of MWNTs, 0.05 g of acetylene black, 0.5 g of Na2SO4, 3.0 g of 10% PTFE, and 5.0 mL of ethanol was used. The stainless steel screen of 200 meshes as current collector was fist pretreated 0.5 h at 80–90°C by 1 L mixed alkaline solution that contained 20 g NaOH, Na3PO4, and Na2CO3 and then was pretreated 0.5 h by 0.5 mol/L hydrochloric acid solutions. Finally, catalyst layer, stainless steel screen, and gas-diffusion layer were cold pressed at 10 MPa for 1 min. The resulting electrode was then cut to 5 cm × 6 cm and about 0.4 mm thick.

2.2. Procedures

Electrolysis was conducted in the terylene diaphragm cell of 100 mL. The anode was a Ti/RuO2 net (16 cm2) and cathode was a gas-diffusion electrode (16 cm2). A schematic of the experimental setup was shown in Figure 1. The electric power was provided by a laboratory direct current power supply with current-voltage monitor. CO2 was bubbled into the electrolyte for 30 min before the reaction. The gas-diffusion electrode was fed with CO2 continually during electrolysis. The distance between anode and cathode was 2 cm. Series concentrations of KHCO3 were chosen as electrolytes to investigate the suitable concentration of electrolytes. The reduction of CO2 was investigated in 0.1 mol/L, 0.3 mol/L, 0.5 mol/L, 0.8 mol/L, and 1.0 mol/L KHCO3 electrolyte at 25°C. The electrolysis voltages were 1 V, 2 V, 3 V, 4 V, and 5 V. During the preparative electrolysis, samples were taken (in 5 min periods) with a volume of 1 mL from the electrolyte in the middle of the reactor.

2.3. Analytical Methods

The XRD patterns were used to discern the identity of any phase present and their crystallite size. The Pd-MWNTs catalyst was characterized by XRD with a Rigaku D/max-III X-ray power diffractometer using Cu Kα radiation with a Ni filter. The distribution of loaded palladium and catalyst morphology were obtained by transmission electron microscope (TEM) on a JEM-2010F transmission electron microscope (TEM) operated at an accelerating voltage of 200 kV. The surface composition of catalyst and Pd surface concentration were then investigated by XPS on PHI5300 Electron Spectrometer (Mg Ka radiation; hv = 1253.6 eV). XPS data were calibrated using the binding energy of C1s (284.6 eV) as the standard. Fourier transform infrared spectroscopy (FTIR) was used to analyses change of functional groups of MWNTs by Excalibur 3100. Spectra were obtained in an optical range of 1000–2000 cm−1 at a resolution of 0.2 cm−1. The cyclic voltammetry (CV) was recorded using a potentiostat/galvanostat (EG&G Model 273A) with a standard three-compartment cell consisting of a Pt wire as a counter electrode, a Ag/AgCl electrode as a reference electrode, and the Pd/MWNTs catalyst modified electrode as a working electrode. The Pd/MWNTs catalyst modified electrodes were made according to previous report [26]. 0.5 mol/L KHCO3 solutions were used as electrolytes, which were saturated with CO2 (N2) to the cell for 30 min before the electrochemical measurements, and gas was continued throughout the electrolysis. The temperature was kept constant at 25°C during the experiment. The scanning rate was 100 mV/s. Soluble products were determined using an ion chromatograph (DIONEX ICS3000) analyses by comparing the retention time of the standard reference compounds. The separation was performed using an AS-11 column at the flow rate of 1.2 mL/min with 250 mmol/L NaOH as the mobile phase at 30°C. The total run time was 15 min and an injection volume is 10 μL.


3. Results and Discussion
3.1. Characterization of Pd-MWNTs Catalyst
3.1.1. FTIR of Pretreatment MWNTs

To disperse metal catalysts on the surface of MWNTs, the modification of MWNTs that could induce the chemical reaction reactive sites must be done first. Mixed acid oxidization of NTs was used to produce functional groups. The typical FTIR spectra of MWNTs and MWNTs pretreated with mixed acid are showed in Figure 2. The MWNTs had two characteristic infrared absorption peaks at 1625 cm−1 and 1575 cm−1. The peak at 1575 cm−1 corresponded to the E1u vibrational modes of carbon nanotubes wall that indicated the presence of graphite structure of MWNTs. The peak at 1384 cm−1 originated from the O–H bending vibration of –COOH, but the peak shape was not very clear, indicating that there were few carboxyl groups on the surface of untreated MWNTs. As showed in the FTIR spectra of MWNTs pretreated with mixed acid, the introduction of −COOH could be observed from the peak 1732 cm−1 that corresponded to the –C=O stretching frequencies. These functional groups played a key role in depositing palladium on the surface of MWNTs and their intensities were greatly enhanced after mixed functionalization [26]. There were electrostatic adsorptions or coordination effect between palladium chloride and functional groups on the surface of MWNTs. Then palladium chloride was reduced by ethylene glycol and the palladium nanoparticles were formed on the surface of MWNTs in situ.

3.1.2. XRD and TEM Analysis of Pd-MWNTs Catalyst

The XRD patterns of Pd-MWNTs catalysts are shown in Figure 3. The main characteristic peak emerged at 39.2° corresponding to the Pd particle, which indicated the successful reduction of metal salt [27]. The Pd peak became narrower and sharper with the increasing diameter of Pd particles. XRD analysis showed that there was no detectable crystal structure of Pd particles over the 1 wt.% Pd-MWNTs catalyst. This result indicated that Pd particles in 1 wt. % Pd-MWNTs were amorphous. The diffraction peaks at 26°, 42.8°, and 54.5° observed in the diffraction of MWNTs could be attributed to the hexagonal graphite structures (002), (100), and (004) [28], respectively, which demonstrated that modified MWNTs still had a high electrical conductivity as original one after oxidation and reduction and thus could be good supporting materials.

Figure 4 presented a TEM image of MWNTs that were covered with Pd nanoparticles. Together with the XRD pattern, these observations suggested that Pd nanoparticles were amorphous and highly dispersed over MWNTs. There was no obvious aggregation on the image. The average particle size was 5.7 nm. A lot of Pd particles were formed in the port and bend part of MWNTs, where defective sites and foundation groups were easily formed after nitro-sulfuric acid treatment.

3.1.3. Electrochemical Analysis of Pd-MWNTs Catalyst

In order to elucidate the catalytic function of Pd-MWNTs composites, cyclic voltammogram for MWNTs and Pd-MWNTs by catalyst modified glassy carbon electrode in 0.5 mol/L KHCO3 solution are shown in Figure 5.

As shown in Figure 5, the cathodes currents obtained under 1 atm N2 were suppressed compared with those obtained under 1 atm CO2. No significant responses beyond the background current were observed for MWNTs and Pd-MWNTs modified glassy carbon electrode under N2 purging condition. Under CO2 purging condition, MWNTs and Pd-MWNTs modified glassy carbon electrode showed reduction peaks at ca. −0.65 V and −0.52 V, respectively. These results indicated that CO2 could take part in the reduction reaction directly. It could be inferred from the fact that CO2 was one key point of the reaction. By bubbling gas through the electrolyte and checking out the change of partial current density resulted from products formation, Hori [29] found that HCO3 was not an electroactive species, assuming that HCO3 was first decomposed to CO2 and CO2 was reduced at the electrode afterwards. The whole reaction process was as follows: CO2 was converted into HCO3 first and then was transport to the surface of palladium nanoparticles in the form of HCO3; HCO3 was decomposed to CO2 and CO2 was reduced at the electrode at last. The CO2 could be chemisorbed as a bent CO2δ. Pd has been shown to strongly adsorb CO2 [30]. The electrode metals interacted with carbon or oxygen coordination or mixed coordination adsorption mode, respectively. It is well known that the decomposition rate of HCO3 is slow in ambient temperature and pressure, so the decompose of HCO3 was the rate determining step in the reaction. Moreover, the reduction current peak of the Pd-MWNTs modified electrode was more positive and higher than that of MWNTs modified electrode under 1 atm CO2. It indicated that Pd-MWNTs catalysts showed high catalytic performance in the electrochemical reduction of CO2.

3.2. Electrochemical Reduction of CO2 to Organic Acids at Pd-MWNTs Gas-Diffusion Electrodes

The influences of electrolysis voltage, reaction time, and electrolyte concentration were discussed, and relations between reaction conditions and products formed were presented. The products distributions and influencing factors were discussed blow.

3.2.1. Role of Electrolyte Concentration

Most of the works were carried out in the aqueous electrolyte of KHCO3, but the concentrations were different, ranged from 0.1 to 0.5 mol/L [10, 16]. The electrode voltage was 4 V and electrolysis time was 20 min. Figure 6 shows the correlation between the KHCO3 concentrations, partial current, and current efficiency at the Pd-MWNTs gas-diffusion electrode for the reductions of CO2. Formic acid and acetic acid were the main products.

As shown in Figure 6, high concentration of electrolytes enhanced the conductivity of the solution. The current densities of formic acid and acetic acid increased with the increasing electrolyte in a certain range. The current density of formic acid reached up to 1.8 mA/cm2 in the 0.5 mol/L KHCO3 electrolytes. The highest current density of acetic acid was 2.13 mA/cm2, which was obtained from 0.8 mol/L KHCO3 solutions. The same trends have taken place in current efficiencies of formic acid (33.8%) and acetic acid (35.3%). The total current efficiency of 0.5 mol L−1 KHCO3 electrolyte 55.4% was the highest, followed by 0.8 mol/L KHCO3 electrolytes 49.9%.

The CO2 reduction was greatly limited by the low solubility and mass transfer of CO2 [31]. The kinetic control was likely to be related to the release of free molecular CO2 from aqueous bicarbonate. The reduction was much affected by decomposition of HCO3. By using the gas diffusion electrodes, a great amount CO2 was bubbled into the electrolyte and reacted with OH. Then CO2 could be carried to the cathode surface more easily in the water-solution ionic solution than across the gas-liquid interface to catalyst surface. The CO2 was chemisorbed by Pd and then reduced to formic acid and acetic acid [30]. Hence, the gas-diffusion electrode increased the reaction rate.

The pH at the electrode was also greatly affected by the electrolyte, since OH was released in the electrode reactions. Hori [29] found that product selectivity depends upon availability of hydrogen or protons on the surface, which was controlled by pH at the electrode. In this experiment, KHCO3 electrolyte with somewhat buffer ability that can neutralize OH and CO2 also acted as both a react ant and a buffer. High pH induced negative electrocatalytic potential for CO2 reduction, which decreased the efficiency of formic acid and acetic acid formation [32]. While high concentration of HCO3 can keep the pH of electrolyte steady, low pH promoted hydrogen evolution in the mean time. Hydrogen evolution reaction also went up with KHCO3 concentration. Hence the current efficiencies of formic acid and acetic acid decreased when high concentration electrolyte was employed.

3.2.2. Influence of Voltage

The voltage and concentration of CO2 reduction products at gas-diffusion electrodes are plotted against the electrode voltage in Figure 7. The formations of formic acid and acetic acid were detected in 0.5 mol/L and 0.8 mol/L KHCO3 solutions, respectively.

As shown in Figure 7, the total current densities gradually increased with the electrode voltages. The total current efficiencies, current densities, and efficiencies of formic acid and acetic acid reached the maximum at 4 V. At this point the maximum current efficiency of formic acid was 33.2%; the maximum current efficiency of acetic acid was 34.8%. The total current efficiencies in 0.5 mol/L and 0.8 mol/L KHCO3 solutions were 54% and 52.6%, respectively. Hence 4 V of electrode voltage was chosen as the optimal voltage for the electrolysis under present conditions.

The reduction of CO2 was a complex multistep reaction [29]. CO2 reduction did not occur easily and the applied electrolysis potentials for CO2 reduction were more negative than the equilibrium value because the single electron reduction of CO2 to CO2•−, which was recognized as the first step to activate CO2 for subsequent reduction steps, occurred at −1.90 V versus NHE due to a large reorganizational energy between liner molecule and bent radical anion. This step has also been determined as the rate determining step for CO2 reduction. As shown in Figure 7, the current densities of formic acid and acetic acid began to rise quickly near 3 V. A large number of CO2•− supply became possible when high voltage was applied.

When the voltage was low, the reaction was controlled by electron transfer obviously. Therefore, with the increase of electrode voltage, the production of formic acid and acetic acid also increased. The formations of formic acid and acetic acid were still controlled by electron transfer when high voltage was employed. The gas-diffusion electrode feeding CO2 to the electrocatalyst contributed to the high electrolysis efficiency [33]. When the voltage was high, hydrogen also formed on the cathode. Hence, further increase of voltage did not increase the current efficiency of organic acid.

3.2.3. Study on Reaction Time

Figure 8 shows the concentration changes of the formed formic acid and acetic acid with the reaction time.

As shown in Figure 8, the current efficiency for formic acid formation increased with increasing the time and reached a maximum of 34.5% at 20 min in 0.5 mol/L KHCO3 electrolytes; the current efficiency for acetic acid formation reached a maximum of 52.3% at 5 min in 0.8 mol/L KHCO3 electrolytes.

It is easier to generate acetic acid as the multielectron transfer reaction of CO2 reduction is thermodynamically conducive to single electron transfer reaction [29]. The numbers of electrons participated in the reaction have a great influence on the product selectivity. When the supply of electron was relatively abundant both in 0.5 mol/L and 0.8 mol/L KHCO3 electrolytes, the formation of acetic is the primary reaction. As shown in Figures 6 and 7, when the voltage was low or the concentration of electrolyte was light, the supply of electron was insufficient. Then, the current efficiency of formic acid is high and its formation was the primary reaction. The current efficiencies declined when the electrolysis time exceeds 20 min. Further electrolysis induced the decomposition of formic acid and acetic acid which competed with the CO2 reduction.

To check the steady of Pd-MWNTs catalysts gas-diffusion electrode, three recycled batches of experiment results were listed below under the same condition (0.5 and 0.8 mol/L KHCO3, 20 min, and 4 V) in Table 1.

The faraday efficiencies of products in 0.5 mol/L KHCO3 electrolytes almost remained unchanged. However the faraday efficiencies of products in 0.8 mol/L KHCO3 electrolytes changed slightly due to complexity caused by high concentration electrolyte. Results indicated that the catalyst remains as high activity and reaction systems keep their steady.

It can be concluded that electrolyte concentration, voltage, and reaction time had considerable influence on the species and amount of the products. High voltage and high concentration electrolyte advanced the formation of acetic acid. The best reaction conditions for the electrochemical reduction of CO2 to acetic acid were 4 V, 5 min and 0.8 mol/L KHCO3. The current efficiencies of acetic acid and formic acid were 52.3% and 8.6%, respectively and the total current efficiency was 60.9%. The best reaction conditions for the electrochemical reduction of CO2 to formic acid were 4 V, 20 min and 0.5 mol/L KHCO3. The current efficiencies of formic acid and acetic acid were 34.5% and 22.4%, respectively; the total current efficiency was is 56.8%.

3.3. Catalysis Analysis of Pd-MWNTs Gas-Diffusion Electrode

Comparisons of faraday efficiencies for the products by electrochemical reduction of CO2 on the MWNTs and Pd-MWNTs gas-diffusion electrode systems are shown in Figure 9.

The electrochemical reduction of CO2 in the Pd-MWNTs gas-diffusion electrode system resulted in a maximum formation of acetic acid with a faraday efficiency of 52.3% and minimum formic acid 8.6% in 0.8 mol/L KHCO3 at 4 V. Acetic acid and formic acid were produced at faradaic efficiency of 22.4% and 34.5%, respectively, in 0.5 mol/L KHCO3 at 4 V. High efficiency and selectivity were achieved when Pd-MWNTs gas-diffusion electrode was employed. The Pd-MWNTs gas-diffusion electrode had high catalytic activity in the reduction of CO2 under the optimal conditions compared with that without Pd nanoparticles. High efficiency attributed to stronger interaction between Pd and MWNTs support. Additionally, Pd catalysts play an important role in the current efficiency and product selectivity.


4. Conclusions

A Pd-MWNTs gas-diffusion electrode was prepared for the electroreduction of CO2. In the fully characterized catalysts, Pd particles of an average size of 5.7 nm were highly dispersed in carbon nanotubes with amorphous structure. The CV behaviors showed that the Pd-MWNTs catalysts promoted the reduction by lowering the reduction potential and increasing the reduction current. In addition, electrochemical reduction of CO2 at Pd-MWNTs gas-diffusion electrodes was investigated in a terylene diaphragm cell. 4 V of electrode voltage was the optimal voltage for the present system. The suitable KHCO3 electrolyte concentrations for the formic acid and acetic acid were 0.5 mol/L and 0.8 mol/L, respectively. The optimum faraday efficiencies of formic and acetic acids formed on the Pd-MWNTs gas-diffusion electrode at 4 V electrode voltages were 34.5% and 52.3%, respectively.


Conflict of Interests

The author declare that there is no conflict of interests regarding the publication of this article.


Acknowledgments

This work was supported by the Fundamental Research Funds for the Central Universities (no. TD2013-2 and 2012LYB33), the National Natural Science Foundation of China (Grant 51278053 and 21373032), the Program for New Century Excellent Talents in University (no. NCET-10-0233), and the Beijing Natural Science Foundation (no. 8122031).


References
1. Pritchard SG. Soil organisms and global climate changePlant PathologyYear: 201160182992-s2.0-78651319300
2. Skorek-Osikowska A,Kotowicz J,Janusz-Szymanska K. Comparison of the energy intensity of the selected CO2-capture methods applied in the ultra-supercritical coal power plantsEnergy and FuelsYear: 2012261165096517
3. Xiaoding X,Moulijn JA. Mitigation of CO2 by chemical conversion: plausible chemical reactions and promising productsEnergy and FuelsYear: 19961023053252-s2.0-0344081139
4. Furler P,Scheffe J,Gorbar M,Moes L,Vogt U,Steinfeld A. Solar thermochemical CO2 splitting utilizing a reticulated porous ceria redox systemEnergy and FuelsYear: 2012261170517059
5. Bocarsly AB,Gibson QD,Morris AJ,et al. Comparative study of imidazole and pyridine catalyzed reduction of carbon dioxide at illuminated iron pyrite electrodesACS CatalysisYear: 20122816841692
6. Whipple DT,Kenis PJA. Prospects of CO2 utilization via direct heterogeneous electrochemical reductionJournal of Physical Chemistry LettersYear: 2010124345134582-s2.0-78650350359
7. Centi G,Perathoner S. Opportunities and prospects in the chemical recycling of carbon dioxide to fuelsCatalysis TodayYear: 20091483-41912052-s2.0-71649086534
8. Pérez-Cadenas AF,Ros CH,Morales-Torres S,Pérez-Cadenas M,Moreno-Castilla PJKC,Kapteijn F. Metal-doped carbon xerogels for the electro-catalytic conversion of CO2 to hydrocarbonsCarbonYear: 201356324331
9. Tripkovic V,Vanin M,Karamad M,et al. Electrochemical CO2 and CO reduction on metal-functionalized porphyrin-like grapheneJournal of Physical Chemistry CYear: 20131171891879195
10. Gonçalves MR,Gomes A,Condeço J,et al. Selective electrochemical conversion of CO2 to C2 hydrocarbonsEnergy Conversion and ManagementYear: 201051130322-s2.0-71049118206
11. Collin JP,Sauvage JP. Electrochemical reduction of carbon dioxide mediated by molecular catalystsCoordination Chemistry ReviewsYear: 19899322452682-s2.0-0001258618
12. Costentin C,Robert M,Savéant JM. Catalysis of the electrochemical reduction of carbon dioxideChemical Society ReviewsYear: 20134262423243623232552
13. Thorson MR,Siil KI,Kenis PJA. Effect of cations on the electrochemical conversion of CO2 to COJournal of the Electrochemical SocietyYear: 20131604G69G74
14. Aytaç A,Gürbüz M,Sanli AE. Electrooxidation of hydrogen peroxide and sodium borohydride on Ni deposited carbon fiber electrode for alkaline fuel cellsInternational Journal of Hydrogen EnergyYear: 2011361610013100212-s2.0-79960914940
15. Hsieh CT,Hung W,Chen W. Electrochemical activity and stability of Pt catalysts on carbon nanotube/carbon paper composite electrodesInternational Journal of Hydrogen EnergyYear: 20103516842584322-s2.0-77955568650
16. Gharibi H,Javaheri M,Kheirmand M,Mirzaie RA. Optimization of the amount of Nafion in multi-walled carbon nanotube/Nafion composites as Pt supports in gas diffusion electrodes for proton exchange membrane fuel cellsInternational Journal of Hydrogen EnergyYear: 2011362013325133342-s2.0-80052922099
17. Jha N,Reddy ALM,Shaijumon MM,Rajalakshmi N,Ramaprabhu S. Pt-Ru/multi-walled carbon nanotubes as electrocatalysts for direct methanol fuel cellInternational Journal of Hydrogen EnergyYear: 20083314274332-s2.0-38449089352
18. Zhao HZ,Chang YY,Liu C. Electrodes modified with iron porphyrin and carbon nanotubes: application to CO2 reduction and mechanism of synergistic electrocatalysisJournal of Solid State ElectrochemistryYear: 201317616571664
19. Yang H,Tu HC,Chiang IL. Carbon cloth based on PAN carbon fiber practicability for PEMFC applicationsInternational Journal of Hydrogen EnergyYear: 2010357279127952-s2.0-77951023912
20. Park S,Lee JW,Popov BN. A review of gas diffusion layer in PEM fuel cells: materials and designsInternational Journal of Hydrogen EnergyYear: 2012377585058652-s2.0-84858283838
21. Jeng KT,Hsu NY,Chien CC. Synthesis and evaluation of carbon nanotube-supported RuSe catalyst for direct methanol fuel cell cathodeInternational Journal of Hydrogen EnergyYear: 2011366399740062-s2.0-79952443738
22. Hsieh C,Hung WM,Chen WY,Lin JY. Microwave-assisted polyol synthesis of Pt–Zn electrocatalysts on carbon nanotube electrodes for methanol oxidationInternational Journal of Hydrogen EnergyYear: 2011364276527722-s2.0-79951580038
23. Kauffman DR,Tang Y,Kichambare PD,Jackovitz JF,Star A. Long-term performance of Pt-decorated carbon nanotube cathodes in phosphoric acid fuel cellsEnergy and FuelsYear: 2010243187718812-s2.0-77950263344
24. Serp P,Corrias M,Kalck P. Carbon nanotubes and nanofibers in catalysisApplied Catalysis AYear: 200325323373582-s2.0-0142062584
25. Wang H,Wang J. Electrochemical degradation of 4-chlorophenol using a novel Pd/C gas-diffusion electrodeApplied Catalysis BYear: 2007771-258652-s2.0-36048974647
26. Felten A,Ghijsen J,Pireaux JJ,et al. Electronic structure of Pd nanoparticles on carbon nanotubesMicronYear: 200940174792-s2.0-5434911624618378149
27. Gao GY,Guo DJ,Li HL. Electrocatalytic oxidation of formaldehyde on palladium nanoparticles supported on multi-walled carbon nanotubesJournal of Power SourcesYear: 20061622109410982-s2.0-33750933912
28. Li W,Liang C,Zhou W,et al. Preparation and characterization of multiwalled carbon nanotube-supported platinum for cathode catalysts of direct methanol fuel cellsJournal of Physical Chemistry BYear: 200310726629262992-s2.0-0037925593
29. Hori Y. Modern Aspects of ElectrochemistryYear: 2008New York, NY, USASpringer
30. Chaplin RPS,Wragg AA. Effects of process conditions and electrode material on reaction pathways for carbon dioxide electroreduction with particular reference to formate formationJournal of Applied ElectrochemistryYear: 20033312110711232-s2.0-0344983917
31. Eggins BR,Bennett EM,McMullan EA. Voltammetry of carbon dioxide—part 2: voltammetry in aqueous solutions on glassy carbonJournal of Electroanalytical ChemistryYear: 19964081-21651712-s2.0-0030147722
32. Gattrell M,Gupta N,Co A. A review of the aqueous electrochemical reduction of CO2 to hydrocarbons at copperJournal of Electroanalytical ChemistryYear: 200659411192-s2.0-33746117239
33. Shibata M,Yoshida K,Furuya N. Electrochemical synthesis of urea at gas-diffusion electrodes: IV. Simultaneous reduction of carbon dioxide and nitrate ions with various metal catalystsJournal of the Electrochemical SocietyYear: 19981457234823532-s2.0-0032122851

Article Categories:
  • Research Article


Previous Document:  Anticancer Activity of Ferulic Acid-Inorganic Nanohybrids Synthesized via Two Different Hybridizatio...
Next Document:  Sufficient condition on the fractional integral for the convergence of a function.