|Effect of the simulated disinfection by microwave energy on the impact strength of the tooth/acrylic resin adhesion.|
|Jump to Full Text|
|PMID: 19088877 Owner: NLM Status: PubMed-not-MEDLINE|
|The objective of this study was to determine the effect of simulated microwave disinfection on the tooth/acrylic resin impact strength. Acrylic molar teeth with a wax stick attached to the ridge lap were included in brass flasks. Specimens were made with Classico thermopolymerized acrylic resin, according to the groups: 1 and 5 - tooth with no treatment (control); 2 and 6 - tooth bur abrasion; 3 and 7 - tooth bur retention; and 4 and 8 - tooth monomer etch. Eighty specimens (n=10) were polymerized in bath cycle at 74( masculine)C for 9 hours and deflasked after flask cooling. Specimen from groups 2, 4, 6 and 8 was submitted to simulated microwave disinfection in a microwave oven at 650W for 3 minutes. Impact strength test was performed with an Otto Wolpert-Werke machine (Charpy system) with an impact load of 40 kpcm. Fracture load value was transformed into impact strength as a function of the bond area (kfg/cm(2)). Collected data were submitted to ANOVA and Tukey's test (alpha=.05) and results indicate that the simulated microwave disinfection decreased the impact strength in all treatments.|
|Rafael L X Consani; Marcelo F Mesquita; Marinaldo H Zampieri; Wilson B Mendes; Simonides Consani|
Related Documents :
|8083837 - Influence of thickness and location on the residual monomer content of denture base cur...
15718807 - Cad generated mold for preoperative implant fabrication in cranioplasty.
7988767 - Impact strength of acrylic resin denture base materials with surface defects.
23307167 - Hpv-16 exposed mouse embryos: a potential model for pregnancy wastage.
24012517 - Quantification of incisal tooth wear in upper anterior teeth: conventional vs new metho...
8705597 - Radiopacity of potential root-end filling materials.
|Type: Journal Article Date: 2008-01-22|
|Title: The open dentistry journal Volume: 2 ISSN: 1874-2106 ISO Abbreviation: Open Dent J Publication Date: 2008|
|Created Date: 2008-12-17 Completed Date: 2011-07-14 Revised Date: 2013-05-23|
Medline Journal Info:
|Nlm Unique ID: 101480503 Medline TA: Open Dent J Country: Netherlands|
|Languages: eng Pagination: 13-7 Citation Subset: -|
|Department of Prosthodontics and Periodontics, Piracicaba Dentistry School, State University of Campinas, Brazil;|
|APA/MLA Format Download EndNote Download BibTex|
Journal ID (nlm-ta): Open Dent J
Journal ID (publisher-id): TODENTJ
Publisher: Bentham Science Publishers Ltd.
2008 Bentham Science Publishers Ltd.
open-access: This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/2.5/), which permits unrestrictive use, distribution, and reproduction in any medium, provided the original work is properly cited.
Received Day: 25 Month: 10 Year: 2007
Accepted Day: 12 Month: 12 Year: 2007
Electronic publication date: Day: 22 Month: 1 Year: 2008
collection publication date: Year: 2008
Volume: 2First Page: 13 Last Page: 17
Publisher Id: TODENTJ-2-13
PubMed Id: 19088877
|Effect of the Simulated Disinfection by Microwave Energy on the Impact Strength of the Tooth/Acrylic Resin Adhesion|
|Rafael L.X. Consani1*|
|Marcelo F. Mesquita2|
|Marinaldo H. Zampieri3|
|Wilson B. Mendes4|
1Department of Prosthodontics and Periodontics, Piracicaba Dentistry School, State University of Campinas, Brazil;
2Department of Prosthodontics and Periodontics, Piracicaba Dentistry School, State University of Campinas, Brazil;
3Piracicaba Dentistry School, State University of Campinas, Brazil
4Department of Clinics, Itauna University Dentistry School, MG, Brazil
5Department of Restorative Dentistry, Piracicaba Dentistry School, State University of Campinas, Brazil.
|*Faculdade de Odontologia de Piracicaba, UNICAMP, Av. Limeira, 901, 13414-903 - Piracicaba, SP, Brazil; Tel: (55) 19- 21065296; E-mail: firstname.lastname@example.org
In addition to the contamination caused during manufacture or manipulation, or by patients, prostheses can be contaminated by microorganisms during clinical use. In an effort to eliminate or decrease cross-contamination, prostheses should be disinfected with suitable chemical solutions [1,2].
Studies have shown that sterile prostheses are contaminated during polishing with pumice slurry or by microorganisms transferred from other prostheses during cloth wheel polishing procedures used in common laboratory practice [3,4].
Methods for prosthesis chemical disinfection have been suggested by many authors to avoid the cross-contamination promoted by pathogenic agent dissemination, including the use of glutaraldehyde, sodium hypochlorite, iodoform, chlorine dioxide or alcohol solutions [5-7].Chemical disinfection, however, does have some disadvantages, such as prosthesis staining and oral tissue reactions in the patient [8-9].
To minimize the disadvantages of chemical disinfection, the use of microwave energy has been suggested as a simple alternative to prosthesis disinfection, with lower operational costs and ease of use . Microwave energy was originally used for the thermally-activated acrylic resin polymerization [11,12];however, the irradiation of resilient linings and acrylic resins immersed in water in a domestic microwave oven effectively sterilizes specimens contaminated by the fungi , Candida albicans or Staphylococcus aureus .
Due to the probability that the acrylic resin denture base is contaminated both internally and externally , the use of microwave energy has been recommended as an ideal method for disinfection [8,9].
The effects of microwave disinfection on hardness or flexural strength of the acrylic resin ,and on the dimensional accuracy of the denture base  have shown that the results were not significantly altered by the disinfection procedure. Microwave post-polymerization irradiation can also be an effective method for increasing the flexural strength of denture relining resins .A recent study demonstrated that simulated disinfection by microwave energy improved denture base adaptation when the traditional clamp flask closure method was used .
Fracture of the tooth/denture base bond may be caused by excessive stress or by fatigue. A poor laboratory technique that impedes a satisfactory bond between tooth and base resin can also be responsible for many failures .Imperceptible traces of wax, not removed by methods of wax elimination, seem to be the principal contaminant and have a highly significant detrimental effect on the bond, causing consequent adhesive failure [17,18]. Changes in the surface of the glossy ridge-lap surface by grooving or retention do not make a significant difference when compared with unmodified surfaces [19,20], while a significant increase in bond strength is obtained when suitable bonding agents are applied .
Studies have been developed with the purpose of demonstrating the influence of mechanical retentions on glossy ridge laps [22,23], and the monomer etching effect on the unmodified ridge laps [24-25] in the adhesive strength between tooth and denture base. In addition, few studies had been developed with the aim of characterizing the effect of microwave disinfection on the impact strength of the tooth/base resin adhesion, a condition that may modify the denture?s durability during oral use.
The purpose of the present study was to verify the effect of simulated microwave disinfection on the impact strength of the tooth/acrylic resin adhesion, when the glossy ridge laps were unmodified, abraded, grooved or etched by monomer. The research hypothesis tested was that the tooth/resin bond would be adversely affected by simulated microwave disinfection, independently of the different treatments to the glossy ridge laps. It may be speculated that the stiffness of the acrylic resin irradiated by microwave energy could be increased, resulting in decreased bond strength in the tooth-resin adhesion.
Wax rectangular mold patterns were poured into each traditional brass flask (Safrany; Safrany Metallurgy, Sao Paulo, SP, Brazil) with type III dental stone (Herodent; Vigodent, Rio de Janeiro, RJ, Brazil), proportioned and manipulated according to the manufacturer?s instructions. After wax pattern removal, the rectangular stone mold was filled with a layer of laboratory silicone putty (Zetalabor; Zhermack, Rovigo, Italy) hard type (85 shore A). Identical shape and size model 34L acrylic molar teeth (Biotone; Dentsplay, Petr?polis, RJ, Brazil), attached with a wax stick (6mm in diameter and 20mm in length) at the ridge lap surface, were partially placed into the silicone layer. The resultant wax stick and attached tooth set was covered with laboratory silicone putty (Zetalabor; Zhermack, Rovigo, Italy). After dental stone isolation with petroleum jelly, the flask was completely poured with type III dental stone (Herodent; Vigodent, Rio de Janeiro, RJ, Brazil) and pressed in a hydraulic press (Linea H; Linea, Sao Paulo, SP, Brazil)for 1 hour.
After pressing, the tooth/wax stick set was deflasked and the wax stick removed from the tooth. The tooth was brushed with hot water and liquid household detergent (Bombril; Bombril-Cirio, S?o Paulo, SP, Brazil) solution to eliminate the wax sticks residues and rinsed with running water. Five specimens (Fig. 1) were made in each flask with the tooth attached to the denture base acrylic resin, proportioned and manipulated according to the manufacturer? instructions, using one of the following protocols:
1? tooth without treatment (control); 2- glossy ridge lap grinding with bur; 3- glossy ridge lap grooving with bur; 4- glossy ridge lap etched by monomer applied for 30 seconds with a small brush before packing .
The specimens of the protocols 5, 6, 7 and 8 were made similarly to protocols 1, 2, 3 and 4 with exception they were submitted afterwards to simulated microwave disinfection in a domestic microwave oven (Continental; Continental Domestic Lines, Manaus, AM, Brazil) for 3 minutes at 650W . For this procedure the specimens were immersed individually in 150mL of distilled water in a glass container. The specimen was removed from the glass container with a tweezers after water cooling at room temperature, and dried with air before impact strength test.
The acrylic resin (Classico; Classico Dental Products, Sao Paulo, SP, Brazil) was prepared using a solution with a ratio of 35.5g polymer to 15mL monomer, according to manufacturer?s instructions. The flasks were placed in traditional clamps after final pressing in a hydraulic press(Linea H; Linea, Sao Paulo, SP, Brazil) under a load of 1,250 kgf for 5 minutes. Eighty specimens (n=10) were conventionally packed, polymerized in a water bath at 740C for 9 hours in a polymerizing unit (Termotron; Piracicaba, Sao Paulo, SP, Brazil)), deflasked after flask cooling at room temperature, and finished with abrasive stones.
The bond impact strength test was measured in the non-disinfected (control) and submitted to simulated microwave disinfection specimens in an impact machine (Wolpert; Otto Wolpert-Werke, Ludwigshafen/Rhein, Germany), using the Charpy system with an impact load of 40 kpcm. The impact strength (kgf/cm2) was calculated as a function of the load applied at the moment of specimen failure (kpcm) and tooth/resin bonding area, using the equation:
IS = F / ?.r2 where:
IS = Impact strength (kgf/cm2).
F = Failure load (kpcm).
?.r2 = tooth/resin bonding area; where: ? = 3.1416 and r2 = 0.09cm2; thus, 0.09x3.1416=0.28cm2.
Observation of the failure mode after impact strength test was under an optical microscope (EMZ-TR; Meiji Thecno Co., Tokyo, Japan), with 1.5x magnification.
Data were submitted to 2-way analysis of variance (SANEST ? Statistical Analysis System), considering 2 factors (ridge lap treatment and simulated microwave disinfection) and their interactions. Since same-factor interactions were significant, differences were submitted to multiple comparison testing (Tukey HSD test at ?=.05).
Two-way ANOVA (Table 1) revealed significant differences in the tooth/resin bond impact strength for the different treatments (p<.00001), and simulated microwave disinfection (p<.00001), and their interactions (p<.00001).
Impact strength means following the use, or not, of microwave disinfection are shown in the Table 2. In the non-disinfected specimens, control and monomer etching presented lower means, but were statistically different when compared to bur abrasion and bur grooving treatments (no statistically significant difference for these latter treatments). In the disinfected specimens, control and monomer etching presented the lowest means and were statistically significantly different when compared to bur abrasion and bur grooving treatments, both with statistically significant difference. When the non-disinfected and disinfected specimens were compared, all treatments demonstrated means with statistically significant difference and were lower in the specimens submitted to disinfection.
In all groups, the predominant failure was mixed (adhesive, and cohesive in the acrylic resin). Mixed failure (adhesive, and cohesive in the tooth) was only showed in 3 specimens, and not any adhesive failure was observed.
In the present in vitro study, the research hypothesis that the tooth/resin bond would be adversely affected by simulated microwave disinfection, independently of the different glossy ridge lap treatments was accepted. The 2-way ANOVA revealed significant difference in the impact strength for the different ridge lap treatments and microwave disinfection. The interactions between treatment and disinfection were also significant (Table 1). Independently of the microwave disinfection, control and monomer etched specimens demonstrated lower means that were statistically different when compared to bur abrasion and bur grooving treatments, both showing no statistically significant difference (Table 2).
Although wax appears to be the principal contaminant and cause of adhesive failure of the tooth-base resin bond [17,18], the denture base material and denture tooth selected may influence the tensile bond strength of the tooth to the base . Physical modification by retention grooves of different shapes on the tooth surface had no significant effect on the bond strength [22, 28], and grinding of the tooth may only be beneficial to bonding in the absence of wax traces . For preventing such failures, the use of modern synthetic detergents that effectively remove all traces of wax is necessary . Detergent solution was used in this study to remove the traces of wax from the teeth. Thus, it may be speculated that the statistical significance showed may be due to the different treatments performed on the tooth ridge laps.
Previous studies have shown that painting with monomer or grinding the ridge lap of the tooth before packing did not seem to improve the adhesion to the resin base [18,25]. Conversely, the present investigation showed that findings from these treatments were not similar. So, results from control and monomer etched specimens were statistically similar, and bur abrasion as well as bur grooving specimens significantly improved the tooth/resin bond (Table 2).
In the present study, the similarity of the impact strength values for control and monomer etched specimens was probably due to the cross-linking added to the methylmetacrylate denture teeth for improving surface hardness and abrasion resistance . This procedure, however, results in decreased bond strength as compared to acrylic resin teeth with no cross-linking . It was showed that when the hardness of the tooth is increased, the bonding strength between the tooth and the denture base decreases .
Chemical interaction of the acrylic resin and ridge lap portion of the tooth influences the bond strength; however, monomer etch had a dramatic effect, decreasing the failure load when the tooth was painted with monomer alone  or when a highly cross-linked denture tooth was used . Different tooth surface modifications resulted in significantly different bond strengths . The mechanical retention, in the form of a grind or groove placed in the ridge lap of the tooth, increased the impact strength values (Table 2). The finding of this investigation is in agreement with classic studies evaluating the bonding of the denture teeth to the acrylic resin base, where mechanical retention was used on the ridge lap [20,22,24,31]. Thus, bur abrasion and bur grooving presented impact strength values that were not statistically significantly different.
It has been suggested that a tooth rough surface may trap wax residues, decreasing the bond strength , whereas an evaluation of the fractured sample showed that the resin mass does not penetrate into the groove made on the ridge lap of the tooth . Within the limitations of this study, the results presented do not agree with the findings of these cited authors.
Earlier study showed that a visual inspection of the fractured areas did not show the fracture mode, suggesting debonding due to deficient resin mass penetration into the irregularities of the ridge lap. In these treatments, better bond strength was attributed to greater surface area and better penetration of the resin mass to the tooth irregularities . Bur grooving may decrease or increase the bonding strength in similar chemically acrylic resins, and the reason for this apparent controversy is difficult to determine .
Table 2 also shows the influence of microwave disinfection on the tooth/acrylic resin impact strength. Control and monomer etched specimens presented lower means that were statistically different when compared to bur abrasion and bur grooving treatments, both with statistically significant difference. Simulated microwave disinfection led to statistically different values of impact strength for the different mechanical treatments. The highest result, for bur ground specimens, was probably due to the different level of irregularities caused by these procedures.
Regions of the denture base with minimal restriction to additional polymerization shrinkage promoted by microwave energy showed better adaptation to the stone cast . By analogy, it may be theorized that a similar phenomenon occurred on the flat surface of the ridge lap, improving the mechanical retention by resin shrinkage with minimal restriction in the adhesion area. Conversely, the additional contraction of the acrylic resin decreased the retention in the depth area of the groove. This decrease in retention is due to the stress induced into the groove by the additional microwave energy polymerization that is afterwards released. The internal stress released by the microwave disinfection may also cause distortion of the denture resin base [10,12].
When the non-disinfected and disinfected specimens were compared, all ridge lap treatments showed means with statistically significant differences, and all means were lower than those of specimens submitted to disinfection (Table 2). Although flexural strength is not significantly altered by microwave energy, there was a small increase in the acrylic resin hardness. A possible explanation for the increased hardness resulting from microwave disinfection might be the lack of water plasticizing effect occurring in the microwave radiated specimens . Conversely, in this study, the specimens were adversely affected by simulated microwave disinfection, decreasing the bond strength values between tooth and acrylic resin.
Irradiation by microwave energy generates heat inside the acrylic resin , increasing the degree of conversion of autopolymerizing acrylic resins  due to a decreased level of residual monomer . Thus, it may be speculated that the stiffness of the acrylic resin irradiated by microwave energy was increased, resulting in a decreased cohesive strength in the irradiated specimens. This decreased strength was evident in all specimens irradiated by microwave energy.
As specified above for the non-disinfected specimens, greater impact strength was shown in the mechanical retention of the irradiated specimens. Due to the material volume trapped inside the ridge lap groove, the deleterious effect of the decreased cohesive strength on the bonding was more evident than the surface roughness of the ground specimens.
The results of this study show that simulated microwave disinfection may be deleterious to tooth/base resin adhesion. The decrease in bond strength may displace the tooth from the base, either by masticatory load or due to accidental dropping during denture cleaning. Although attempts were made to characterize the effect of microwave irradiation on the tooth/resin bond, this study is limited in predicting the effect of other variables involved in the investigation. Further studies are necessary to evaluate whether the effect of microwave energy on tooth-resin impact strength may be deleterious to the denture base adaptation and stability in oral use.
The failure resulting from the impact strength test was predominantly mixed (adhesive, and cohesive in the acrylic resin). This fact signifies that the cohesive strength of the tooth is greater when compared to the acrylic resin cohesive strength, and the failure of the bond will be probably in the acrylic resin base when the denture is in use.
Within the limitations of this in vitro study, the results suggest that the simulated microwave disinfection significantly decreased the tooth/resin impact strength. Additionally, mechanical retention improved the impact strength when compared to the control and monomer etched treatments; however, the impact load was lower in the disinfected specimens.
This study was supported by PIBIC/CNPq/UNICAMP at Piracicaba Dental School, State University of Campinas, Sao Paulo, Brazil.
|1.||Brace ML,Plummer KD. Practical denture disinfectionJ Prosthet Dent 1993;70:538–40. [pmid: 8277443]|
|2.||Powell GL,Runnells RD,Saxon BA,Whisenant BK. The presence and identification of organisms transmitted to dental laboratoriesJ Prosthet Dent 1990;64:235–7. [pmid: 2202822]|
|3.||Katberg Jr JW. Cross-contamination via the prosthodontic laboratoryJ Prosthet Dent 1974;32:412–9. [pmid: 4606395]|
|4.||Kahn RC,Lancaster MV,Kate W. The microbiologic cross-contamination of dental prosthesesJ Prosthet Dent 1982;47:556–9. [pmid: 6953241]|
|5.||Rudd RW,Senia ES,McCleskey FK,Adams Jr ED. Sterilization of complete dentures with sodium hypochloriteJ Prosthet Dent 1984;51:318–21. [pmid: 6584598]|
|6.||Bell JA,Brockmann SL,Feil P,Sackuvich DA. The effectiveness of two disinfectants on denture base acrylic resin with an organic loadJ Prosthet Dent 1999;61:580–3. [pmid: 2664144]|
|7.||Chau VB,Saunder TR,Pimsler M,Elfring DR. In-depth disinfection of acrylic resinsJ Prosthet Dent 1995;74:09–13.|
|8.||Rohrer MD,Bulard RA. Microwave sterilizationJ Am Dent Assoc 1985;110:194–8. [pmid: 3884686]|
|9.||Baysan A,Whiley R,Wright PS. Use of microwave energy to disinfect a long-term soft lining material contaminated with Candida albicans or Staphylococcus aureusJ Prosthet Dent 1998;79:454–8. [pmid: 9576322]|
|10.||Polyzois GL,Zissis AJ,Yannikakis SA. The effect of glutaraldehyde and microwave disinfection on some properties of acrylic denture resinInt J Prosthodont 1995;8:150–4. [pmid: 7575966]|
|11.||De Clerk JP. Microwave polymerization of acrylic resins used in dental prosthesesJ Prosthet Dent 1987;57:650–8. [pmid: 3298632]|
|12.||Thomas CJ,Webb BC. Microwaving of acrylic resin denturesEur J Prosthodont Restor Dent 1995;3:179–82. [pmid: 8601161]|
|13.||Pavan S,Arioli Filho JN,Dos Santos PH,Mollo Jr FA. Effect of microwave treatments on dimensional accuracy of maxillary acrylic resin denture baseBraz Dent J 2005;16:119–23. [pmid: 16475605]|
|14.||Vergani CE,Seo RS,Pavarina AC,Reis JMSN. Flexural strength of autopolymerizing denture reline resins with microwave post-polymerization treatmentJ Prosthet Dent 2005;93:577–83. [pmid: 15942620]|
|15.||Consani RLX,Mesquita MF,Nobilo MAA,Henriques GEP. Influence of simulated microwave disinfection on complete denture base adaptation using different flask closure methodsJ Prosthet Dent 2007;97:73–8.|
|16.||Huggett R,John G,Jagger RG,Bates JF. Strength of the acrylic denture base tooth bondBr Dent J 1982;00:153–87.|
|17.||Schoonover IC,Fischer TE,Serio AF,Sweeney WT. Bonding of plastic teeth to hest-cured denture base resinsJ Am Dent Assoc 1952;44:285–7. [pmid: 14897613]|
|18.||Spratley MH. An investigation of the adhesion of acrylic resin teeth to denturesJ Prosthet Dent 1987;58:389–92. [pmid: 3305906]|
|19.||Cunningham JL,Benington IC. A new technique for determining the denture tooth bondJ Oral Rehabil 1996;23:202–9. [pmid: 8667127]|
|20.||Cunningham JL,Benington IC. An investigation of the variables which may affect the bond between plastic teeth and denture base resinJ Dent 1999;27:129–35. [pmid: 10071470]|
|21.||Cunningham JL. Shear bond strength of resin teeth to heat-cured and light-cured denture base resinJ Oral Rehabil 2000;27:312–6. [pmid: 10792592]|
|22.||Cardash HS,Liberman R,Helft M. The effect of retention grooves in acrylic resin teeth on tooth denture-base bondJ Prosthet Dent 1986;55:526–8. [pmid: 3514898]|
|23.||Cardash HS,Applebaum B,Liberman R. Effect of retention grooves on tooth-denture base bondJ Prosthet Dent 1990;64:492–96. [pmid: 2231463]|
|24.||Civjan S,Huget EF,Simon LB. Modifications of the fluid resin techniqueJ Am Dent Assoc 1972;85:109–112. [pmid: 4555334]|
|25.||Morrow RM,Matvias FM,Windeler AS,Fuchs RJ. Bonding of plastic teeth to two heat-curing denture base resinsJ Prosthet Dent 1978;39:565–68. [pmid: 349144]|
|26.||Barpal D,Curtis AD,Finzen F,Perry J,Gansky SA. Failure load of acrylic resin denture teeth bonded to high impact acrylic resinsJ Prosthet Dent 1998;80:666–71. [pmid: 9830071]|
|27.||Schneider RL,Curtis ER,Clancy JMS. Tensile bond strength of acrylic resin denture teeth to a microwave- or heat-processed denture baseJ Prosthet Dent 2002;88:145–50. [pmid: 12397241]|
|28.||Saavedra G,Neisser MP,Sinhoreti MAC,Machado C. Evaluation of bond strength of denture teeth bonded to heat polymerized acrylic resin denture basesBraz J Oral Sci 2004;3:458–64.|
|29.||Clancy JM,Boyer DB. Comparative bond strengths of light-cured heat-cured, and autopolymerizing denture resins to denture teethJ Prosthet Dent 1989;61:457–62. [pmid: 2657009]|
|30.||Suzuki S,Sakoh M,Shiba A. Adhesive bonding of denture base resins to plastic denture teethJ Biomed Mater Res 1990;24:1091–103. [pmid: 2203795]|
|31.||Vallittu PK. Bonding of resin teeth to the polymethyl methacrylate denture base materialActa Odontol Scand 1995;53:99–104. [pmid: 7610783]|
|32.||Blagojevic V,Murphy VM. Microwave polymerization of denture base materials. A comparative study J Oral Rehabil 1999;26:804–8. [pmid: 10564437]|
Keywords: Key Words Microwave disinfection, impact strength, tooth/acrylic resin adhesion, glossy ridge lap retention.
Previous Document: A role for non-antimicrobial actions of tetracyclines in combating oxidative stress in periodontal a...
Next Document: The Antimicrobial Effect of Silver Ion Impregnation into Endodontic Sealer against Streptococcus mut...